This work summarizes recent progress on the thermal transport properties of three-dimensional (3D) nanostructures, with an emphasis on experimental results. Depending on the applications, different 3D nanostructures can be prepared or designed to eit
her achieve a low thermal conductivity for thermal insulation or thermoelectric devices, or a high thermal conductivity for thermal interface materials used in the continuing miniaturization of electronics. A broad range of 3D nanostructures have been discussed, ranging from colloidal crystals/assemblies, array structures, holey structures, hierarchical structures, 3D nanostructured fillers for metal matrix composites and polymer composites. Different factors that impact the thermal conductivity of these 3D structures are compared and analyzed. This work provides an overall understanding of the thermal transport properties of various 3D nanostructures, which will shed light on the thermal management at nanoscale.
The titanium fire as produced during high pressure and friction is the major failure scenario for aero-engines. To alleviate this issue, Ti-V-Cr and Ti-Cu-Al series burn resistant titanium alloys have been developed. However, which burn resistant all
oy exhibit better property with reasonable cost needs to be evaluated. This work unveils the burning mechanisms of these alloys and discusses whether burn resistance of Cr and V can be replaced by Cu, on which thorough exploration is lacking. Two representative burn resistant alloys are considered, including Ti14(Ti-13Cu-1Al-0.2Si) and Ti40(Ti-25V-15Cr-0.2Si)alloys. Compared with the commercial non-burn resistant titanium alloy, i.e., TC4(Ti-6Al-4V)alloy, it has been found that both Ti14 and Ti40 alloys form protective shields during the burning process. Specifically, for Ti14 alloy, a clear Cu-rich layer is formed at the interface between burning product zone and heat affected zone, which consumes oxygen by producing Cu-O compounds and impedes the reaction with Ti-matrix. This work has established a fundamental understanding of burning resistant mechanisms for titanium alloys. Importantly, it is found that Cu could endow titanium alloys with similar burn resistant capability as that of V or Cr, which opens a cost-effective avenue to design burn resistant titanium alloys.