SmB6 has been predicted and verified as a prototype of topological Kondo insulators (TKIs). Here we report longitudinal magnetoresistance and Hall coefficient measurements on co-sputtered nanocrystalline SmB6 films and try to find possible signatures
of their topological properties. The magnetoresistance (MR) at 2 K is positive and linear (LPMR) at low field and becomes negative and quadratic at higher field. While the negative part is known from the reduction of the hybridization gap due to Zeeman splitting, the positive dependence is similar to what has been observed in other topological insulators (TI). We conclude that the LPMR is a characteristic feature of TI and is related to the linear dispersion near the Dirac cone. The Hall resistance shows a sign change around 50 K. It peaks and becomes nonlinear at around 10 K then decreases below 10 K. This indicates that carriers with opposite signs emerge below 50 K. Two films with different geometries (thickness and lateral dimension) show contrasting behavior below and above 50K, which proves the surface origin of the low temperature carriers in these films. The temperature dependence of magnetoresistance and the Hall data indicates that the surface states are likely non-trivial.
Topological insulators are a class of materials with insulating bulk but protected conducting surfaces due to the combination of spin-orbit interactions and time-reversal symmetry. The surface states are topologically non-trivial and robust against n
on-magnetic backscattering, leading to interesting physics and potential quantum computing applications1, 2. Recently there has been a fast growing interest in samarium hexboride (SmB6), a Kondo insulator predicted to be the first example of a correlated topological insulator3, 4. Here we fabricated smooth thin films of nanocrystalline SmB6 films. Their transport behavior indeed shows that SmB6 is a bulk insulator with topological surface states. Upon decreasing the temperature, the resistivity r{ho} of Sm0.14B0.86 (SmB6) films display significant increase below 50 K due to hybridization gap formation, and it shows a saturation behavior below 10 K. The saturated resistance of our textured films is similar to that of the single crystals, suggesting that this conduction is from the surface and robust against grain boundary scatterings. Point contact spectroscopy (PCS) of the film using a superconducting tip displays both a Kondo Fano resonance and Andreev reflection, suggesting the existence of both an insulating Kondo lattice and metallic surface states.