The crystal structures of LaAlO3 films grown by pulsed laser deposition on SrTiO3 substrates at oxygen pressure of 10-3 mbar or 10-5 mbar, where kinetics of ablated species hardly depend on oxygen background pressure, are compared. Our results show t
hat the interface between LaAlO3 and SrTiO3 is sharper when the oxygen pressure is lower. Over time, the formation of various crystalline phases is observed while the crystalline thickness of the LaAlO3 layer remains unchanged. X-ray scattering as well as atomic force microscopy measurements indicate three-dimensional growth of such phases, which appear to be fed from an amorphous capping layer present in as-grown samples.
We report comprehensive x-ray diffraction studies of the crystal structure and epitaxy of thin films of the topological insulator Bi2Te3 grown on Si (1 1 1). The films are single crystals of high crystalline quality, which strongly depends on that of
their substrates, with in-plane epitaxial relationships of Bi2Te3 [2 1 -3 0] || Si [1 -1 0] and Bi2Te3 [0 1 -1 0] || Si [1 1 -2] along which the lattices of 1x3 Bi2Te3 and 2x2 Si supercells are well matched. As the samples age, we observe loss of crystalline Bi2Te3 film thickness accompanied with roughening of the crystalline interfaces, formation of new crystalline phases as well as compositional and structural modification of the Si substrate, consistent with the diffusion of Te into the Si substrate.