Atomic layer deposition was used to synthesize niobium silicide (NbSi) films with a 1:1 stoichiometry, using NbF5 and Si2H6 as precursors. The growth mechanism at 200oC was examined by in-situ quartz crystal microbalance (QCM) and quadrupole mass spe
ctrometer (QMS). This study revealed a self-limiting reaction with a growth rate of 4.5 {AA}/cycle. NbSi was found to grow only on oxide-free films prepared using halogenated precursors. The electronic properties, growth rate, chemical composition, and structure of the films were studied over the deposition temperature range 150-400oC. For all temperatures, the films are found to be stoichiometric NbSi (1:1) with no detectable fluorine impurities, amorphous with a density of 6.65g/cm3, and metallic with a resistivity {rho}=150 {mu}{Omega}.cm at 300K for films thicker than 35 nm. The growth rate was nearly constant for deposition temperatures between 150-275oC, but increases above 300oC suggesting the onset of non-self limiting growth. The electronic properties of the films were measured down to 1.2K and revealed a superconducting transition at Tc=3.1K. To our knowledge, a superconducting niobium silicide film with a 1:1 stoichiometry has never been grown before by any technique.