The anisotropic magnetic properties of the antiferromagnetic compound CePd$_2$Ge$_2$, crystallizing in the tetragonal crystal structure have been investigated in detail on a single crystal grown by Czochralski method. From the electrical transport, m
agnetization and heat capacity data, the N{e}el temperature is confirmed to be 5.1 K. Anisotropic behaviour of magnetization and resistivity is observed along the two principal crystallographic directions viz., [100] and [001]. The isothermal magnetization measured in the magnetically ordered state at 2 K exhibits a spin re-orientation at 13.5 T for field applied along [100] direction, whereas the magnetization was linear along the [001] direction attaining a value of 0.94 $mu_{rm B}$/Ce at 14 T. The reduced value of the magnetization is attributed to the crystalline electric field (CEF) effects. A sharp jump in the specific heat at the magnetic ordering temperature is observed. After subtracting the phononic contribution, the jump in the heat capacity amounts to 12.5 J/K mol which is the expected value for a spin ${1}{2}$ system. From the CEF analysis of the magnetization data the excited crystal field split energy levels were estimated to be at 120 K and 230 K respectively, which quantitatively explain the observed Schottky anomaly in the heat capacity. A magnetic phase diagram has been constructed based on the field dependence of magnetic susceptibility and the heat capacity data.
We present here magnetization, specific heat and Raman studies on single-crystalline specimens of the first pyrochlore member $Sm_2Ti_2O_7$ of the rare-earth titanate series. Its analogous compound $Sm_2Zr_2O_7$ in the rare-earth zirconate series is
also investigated in the polycrystalline form. The Sm spins in $Sm_2Ti_2O_7$ remain unordered down to at least T = 0.5 K. The absence of magnetic ordering is attributed to very small values of exchange ($theta_{cw} ~ -0.26 K$) and dipolar interaction ($mu_{eff} ~ 0.15 mu_B$) between the $Sm^{3+}$ spins in this pyrochlore. In contrast, the pyrochlore $Sm_2Zr_2O_7$ is characterized by a relatively large value of Sm-Sm spin exchange ($theta_{cw} ~ - 10 K$); however, long-range ordering of the $Sm^{3+}$ spins is not established at least down to T = 0.67 K, due to frustration of the $Sm^{3+}$ spins on the pyrochlore lattice. The ground state of $Sm^{3+}$ ions in both pyrochlores is a well-isolated Kramers doublet. The higher-lying crystal field excitations are observed in the low-frequency region of the Raman spectra of the two compounds recorded at T = 10 K. At higher temperatures, the magnetic susceptibility of $Sm_2Ti_2O_7$ shows a broad maximum at T = 140 K while that of $Sm_2Zr_2O_7$ changes monotonically. Whereas $Sm_2Ti_2O_7$ is a promising candidate for investigating spin-fluctuations on a frustrated lattice as indicated by our data, the properties of $Sm_2Zr_2O_7$ seem to conform to a conventional scenario where geometrical frustration of the spin exclude their long-range ordering.
We have successfully grown the single crystals of CeAg$_2$Ge$_2$, for the first time, by flux method and studied the anisotropic physical properties by measuring the electrical resistivity, magnetic susceptibility and specific heat. We found that CeA
g$_2$Ge$_2$ undergoes an antiferromagnetic transition at $T_{rm N}$ = 4.6 K. The electrical resistivity and susceptibility data reveal strong anisotropic magnetic properties. The magnetization measured at $T$ = 2 K exhibited two metamagnetic transitions at $H_{rm m1}$ = 31 kOe and $H_{rm m2}$ = 44.7 kOe, for $H parallel$ [100] with a saturation magnetization of 1.6 $mu_{rm B}$/Ce. The crystalline electric field (CEF) analysis of the inverse susceptibility data reveals that the ground state and the first excited states of CeAg$_2$Ge$_2$ are closely spaced indicating a quasi-quartet ground state. The specific heat data lend further support to the presence of closely spaced energy levels.