Helicity-dependent photocurrent delta-I has been detected successfully under experimental configuration that a circularly polarized light beam is impinged with a right angle on a cleaved sidewall of the Fe/x-AlOx/GaAs-based n-i-p double-heterostructu
re. The photocurrent delta-I has showed a well-defined hysteresis loop which resembles that of the magnetization of the in-plane magnetized Fe layer in the devices. The value of delta-I has been |delta-I|~0.2 nA at 5 K under the remnant magnetization state. Study on temperature dependence of the relative delta-I value at H = 0 has revealed that it is maximized at temperatures 125 - 150 K, and is still measurable at room temperature.
Fabrication and optical characteristics of a spin light-emitting-diode (spin-LED) having dual spin-injection electrodes with anti-parallel magnetization configuration are reported. Alternating a current between the two electrodes using a PC-driven cu
rrent source has led us to the observation of helicity switching of circular polarization at the frequency of 1 kHz. Neither external magnetic fields nor optical delay modulators were used. Sending dc-currents to both electrodes with appropriate ratio has resulted in continuous variation of circular polarization between the two opposite helicity, including the null polarization. These results suggest that the tested spin-LED has the feasibility of a monolithic light source whose circular polarization can be switched or continuously tuned all electrically.
We report that an ultra-thin, post-oxidized aluminum epilayer grown on the AlGaAs surface works as a high-quality tunnel barrier for spin injection from a ferromagnetic metal to a semiconductor. One of the key points of the present oxidation method i
s the formation of the crystalline AlOx template layer without oxidizing the AlGaAs region near the Al/AlGaAs interface. The oxidized Al layer is not amorphous but show well-defined single crystalline feature reminiscent of the spinel gamma-AlOx phase. A spin-LED consisting of an Fe layer, a crystalline AlOx barrier layer, and an AlGaAs-InGaAs double hetero-structure has exhibited circularly polarized electroluminescence with circular polarization of P_{EL} = 0.145 at the remnant magnetization state of the Fe layer, indicating the relatively high spin injection efficiency (epsilon = 2P_{EL} / P_{Fe}) of 0.63.