Glassy magnetic phase driven by short range charge and magnetic ordering in nanocrystalline La$_{1/3}$Sr$_{2/3}$FeO$_{3-delta}$: Magnetization, Mossbauer, and polarised neutron studies

The charge ordered La$_{1/3}$Sr$_{2/3}$FeO$_{3-delta}$ (LSFO) in bulk and nanocrystalline forms are investigated using ac and dc magnetization, M{o}ssbauer, and polarised neutron studies. A complex scenario of short range charge and magnetic ordering is realized from the polarised neutron studies in nanocrystalline specimen. This short range ordering does not involve any change in spin state and modification in the charge disproportion between Fe$^{3+}$ and Fe$^{5+}$ compared to bulk counterpart as evident in the M{o}ssbauer results. The refinement of magnetic diffraction peaks provides magnetic moments of Fe$^{3+}$ and Fe$^{5+}$ are about 3.15$mu_B$ and 1.57$mu_B$ for bulk, and 2.7$mu_B$ and 0.53$mu_B$ for nanocrystalline specimen, respectively. The destabilization of charge ordering leads to magnetic phase separation, giving rise to the robust exchange bias (EB) effect. Strikingly, EB field at 5 K attains a value as high as 4.4 kOe for average size $sim$ 70 nm, which is zero for the bulk counterpart. A strong frequency dependence of ac susceptibility reveals cluster-glass like transition around $sim$ 65 K, below which EB appears. Overall results propose that finite size effect directs the complex glassy magnetic behavior driven by unconventional short range charge and magnetic ordering, and magnetic phase separation appears in nanocrystalline LSFO.

Exchange bias effect in the phase separated Nd_{1-x}Sr_{x}CoO_3 at the spontaneous ferromagnetic/ferrimagnetic interface

We report the new results of exchange bias effect in Nd_{1-x}Sr_{x}CoO_3 for x = 0.20 and 0.40, where the exchange bias phenomenon is involved with the ferrimagnetic (FI) state in a spontaneously phase separated system. The zero-field cooled magnetization exhibits the FI (T_{FI}) and ferromagnetic (T_C) transitions at ~ 23 and sim 70 K, respectively for x = 0.20. The negative horizontal and positive vertical shifts of the magnetic hysteresis loops are observed when the system is cooled through T_{FI} in presence of a positive static magnetic field. Training effect is observed for x = 0.20, which could be interpreted by a spin configurational relaxation model. The unidirectional shifts of the hysteresis loops as a function of temperature exhibit the absence of exchange bias above T_{FI} for x = 0.20. The analysis of the cooling field dependence of exchange bias field and magnetization indicates that the ferromagnetic (FM) clusters consist of single magnetic domain with average size around sim 20 and ~ 40 AA ~ for x = 0.20 and 0.40, respectively. The sizes of the FM clusters are close to the percolation threshold for x = 0.20, which grow and coalesce to form the bigger size for x = 0.40 resulting in a weak exchange bias effect.

Exchange bias with Fe substitution in LaMnO_3

The exchange bias (EB) in LaMn_{0.7}Fe_{0.3}O_3 is observed by the negative shift and training effect of the hysteresis loops, while the sample was cooled in external magnetic field. The analysis of cooling field dependence of EB gives the size of the ferromagnetic (FM) cluster ~ 25 Angstrom, where the magnetic anisotropy of FM cluster is found two order of magnitude higher than the FM bulk manganites. We propose that the nanoscale FM clusters are embedded in the glassy magnetic host with EB at the FM/glassy magnetic interface.