We investigate the structure and magnetic properties of thin films of the LaCoO$_{3}$ compound. Thin films are deposited by pulsed laser deposition on various substrates in order to tune the strain from compressive to tensile. Single-phase (001) orie
nted LaCoO$_{3}$ layers were grown on all substrates despite large misfits. The tetragonal distortion of the films covers a wide range from -2% to 2.8%. Our LaCoO$_{3}$ films are ferromagnetic with Curie temperature around 85 K, contrary to the bulk. The total magnetic moment is below $1mu_{B}$/Co$^{3+}$, a value relatively small for an exited spin-state of the Co$^{3+}$ ions, but comparable to values reported in literature. A correlation of strain states and magnetic moment of Co$^{3+}$ ions in LaCoO$_{3}$ thin films is observed.
The magnetization of ferromagnetic LaCoO3 films grown epitaxially on piezoelectric substrates has been found to systematically decrease with the reduction of tensile strain. The magnetization change induced by the reversible strain variation reveals
an increase of the Co magnetic moment with tensile strain. The biaxial strain dependence of the Curie temperature is estimated to be below 4K/% in the as-grown tensile strain state of our films. This is in agreement with results from statically strained films on various substrates.