The transport and complex optical properties of the electron-doped iron-arsenic superconductor BaFe1.85Co0.15As2 with Tc = 25 K have been examined in the Fe-As planes above and below Tc. A Bloch-Gruneisen analysis of the resistivity yields a weak ele
ctron-phonon coupling constant lambda_ph ~ 0.2. The low-frequency optical response in the normal state appears to be dominated by the electron pocket and may be described by a weakly-interacting Fermi liquid with a Drude plasma frequency of omega_p,D ~ 7840 cm-1 (~ 0.972 eV) and scattering rate 1/tau_D ~ 125 cm-1 (~ 15 meV) just above Tc. The frequency-dependent scattering rate 1/tau(omega) has kinks at ~ 12 and 55 meV that appear to be related to bosonic excitations. Below Tc the majority of the superconducting plasma frequency originates from the electron pocket and is estimated to be omega_p,S ~ 5200 cm-1 (lambda0 ~ 3000 Angstroms) for T << Tc, indicating that less than half the free carriers in the normal state have collapsed into the condensate, suggesting that this material is not in the clean limit. Supporting this finding is the observation that this material falls close to the universal scaling line for a BCS dirty-limit superconductor in the weak-coupling limit. There are two energy scales for the superconductivity in the optical conductivity and photo-induced reflectivity at Delta1 ~ 3.1 +/- 0.2 meV and Delta2 ~ 7.4 +/- 0.3 meV. This corresponds to either the gaping of the electron and hole pockets, respectively, or an anisotropic s-wave gap on the electron pocket; both views are consistent with the s+/- model.
The detailed optical properties of BaFe2As2 have been determined over a wide frequency range above and below the structural and magnetic transition at T_N = 138 K. A prominent in-plane infrared-active mode is observed at 253 cm^{-1} (31.4 meV) at 295
K. The frequency of this vibration shifts discontinuously at T_N; for T < T_N the frequency of this mode displays almost no temperature dependence, yet it nearly doubles in intensity. This anomalous behavior appears to be a consequence of orbital ordering in the Fe-As layers.