Magnetic field effect on Fe-induced short-range magnetic correlation and electrical conductivity in Bi$_{1.75}$Pb$_{0.35}$Sr$_{1.90}$Cu$_{0.91}$Fe$_{0.09}$O$_{6+y}$

We report electrical resistivity measurements and neutron diffraction studies under magnetic fields of Bi$_{1.75}$Pb$_{0.35}$Sr$_{1.90}$Cu$_{0.91}$Fe$_{0.09}$O$_{6+y}$, in which hole carriers are overdoped. This compound shows short-range incommensurate magnetic correlation with incommensurability $delta=0.21$, whereas a Fe-free compound shows no magnetic correlation. Resistivity shows an up turn at low temperature in the form of $ln(1/T)$ and shows no superconductivity. We observe reduction of resistivity by applying magnetic fields (i.e., a negative magnetoresistive effect) at temperatures below the onset of short-range magnetic correlation. Application of magnetic fields also suppresses the Fe induced incommensurate magnetic correlation. We compare and contrast these observations with two different models: 1) stripe order, and 2) dilute magnetic moments in a metallic alloy, with associated Kondo behavior. The latter picture appears to be more relevant to the present results.

Incommensurate spin correlations induced by magnetic Fe ions substituted into overdoped Bi1.75Pb0.35Sr1.90CuO6+z

Spin correlations in the overdoped region of Bi1.75Pb0.35Sr1.90CuO6+z have been explored with Fe-doped single crystals characterized by neutron scattering, muon-spin-rotation (muSR) spectroscopy, and magnetic susceptibility measurements. Static incommensurate spin correlations induced by the Fe spins are revealed by elastic neutron scattering. The resultant incommensurability delta is unexpectedly large (~0.2 r.l.u.), as compared with delta ~ 1/8 in overdoped superconductor La2-xSrxCuO4. Intriguingly, the large delta in this overdoped region is close to the hole concentration p. This result is reminiscent of the delta ~ p trend observed in underdoped La2-xSrxCuO4; however, it is inconsistent with the saturation of delta in the latter compound in the overdoped regime. While our findings in Fe-doped Bi1.75Pb0.35Sr1.90CuO6+z support the commonality of incommensurate spin correlations in high-Tc cuprate superconductors, they also suggest that the magnetic response might be dominated by a distinct mechanism in the overdoped region.

Spin and charge orders and their hole-doping dependence in single layered cobaltate La2-xCaxCoO4(0.3<x<0.8)

Neutron scattering experiments were performed on single crystals of layered cobalt-oxides La2-xCaxCoO4 (LCCO) to characterize the charge and spin orders in a wide hole-doping range of 0.3<x<0.8. For a commensurate value of x=0.5 in (H,0,L) plane, two types of superlattice reflections concomitantly appear at low temperature; one corresponds to a checkerboard charge ordered pattern of Co2+/Co3+ ions and the other is magnetic in origin. Further, the latter magnetic-superlattice peaks show two types of symmetry in the reflections, suggesting antiferromagnetic-stacking (AF-S) and ferromagnetic-stacking (F-S) patterns of spins along the c direction. From the hole-doping dependence, the in-plane correlation lengths of both charge and spin orders are found to give a maximum at x=0.5. These features are the same with those of x=0.5 in La1-xSr1+xMnO4 (LSMO), a typical checkerboard and spin ordered compound. However, in (H,H,L) plane, we found a magnetic scattering peak at Q=(1/4,1/4,1/2) position below TN. This magnetic peak can not be understood by considering the Co2+ spin configuration, suggesting that this peak is originated from Co3+ spin order. By analyzing these superlattice reflections, we found that they are originated from high-spin state of Co3+ spin order.

Low Symmetry Phase in (001) BiFeO$_3$ Epitaxial Constrained Thin Films

The lattice of (001)-oriented BiFeO$_3$ epitaxial thin film has been identified by synchrotron x-ray diffraction. By choosing proper scattering zones containing the fixed (001) reflection, we have shown that low-symmetry phases similar to a $M_A$ phase exist in the thin film at room temperature. These results demonstrate a change in phase stability from rhombohedral in bulk single crystals, to a modified monoclinic structure in epitaxial thin films.