Elastic and inelastic neutron scattering measurements have been performed on powder and single-crystal samples of orthorhombic CeRu2Al10. The order forming below T0 = 27 K was identified as a long-range antiferromagnetic state with the wave vector k
= (1,0,0). The magnetic spectral response in the ordered phase, measured on powder, is characterized by a spin gap and a pronounced peak at 8 meV, whose Q dependence suggests a magnetic origin. Both features are suppressed when temperature is raised to T0, and a conventional relaxational behavior is observed at 40 K. This peculiar spin dynamics is discussed in connection with recent magnetization results for the same compound.
The nature of the unconventional ordered phase occurring in CeRu2Al10 below T0 = 27 K was investigated by neutron scattering. Powder diffraction patterns show clear superstructure peaks corresponding to forbidden (h + k)-odd reflections of the Cmcm s
pace group. Inelastic neutron scattering experiments further reveal a pronounced magnetic excitation developing in the ordered phase at an energy of 8 meV.
Neutron powder diffraction measurements have been performed on Ce_xNd_{1-x}B_6 (x = 0.5, 0.6, 0.7, and 0.8) solid solutions to determine the type of magnetic order occurring in these compounds as a result of the interplay between magnetic dipole exch
ange and antiferroquadrupolar interactions. In the Ce-rich range, the sequence of two magnetic phases, with an incommensurate order [k = (1/4 -delta, 1/4 -delta, 1/2)] forming below T N followed by a lock-in--type transition at lower temperature, is quite similar to that reported earlier for Ce_xPr_{1-x} B_6. For x = 0.5, on the other hand, the same antiferromagnetic order as in pure NdB6 first occurs at TN, then coexists with an incommensurate component below the lower transition temperature. These results are in good agreement with previous resistivity measurements and support the idea that Ce and Nd magnetic moments in this system can be relatively decoupled.
Magnetic ordering phenomena in CexPr1-xB6 solid solutions have been studied using both powder and single-crystal neutron diffraction. A variety of magnetic structures are observed depending on temperature and Ce concentration. Over a broad compositio
n range (x $le$ 0.7), Pr-Pr interactions play a dominant role, giving rise to incommensurate structures with wave vectors of the form k{IC1}=(1/4-delta, 1/4, 1/2) or k{IC2}=(1/4-delta, 1/4-delta, 1/2). The crossover to a CeB6-like regime takes place near x = 0.7-0.8. For the latter composition, the antiferroquadrupolar phase transition observed in transport measurements precedes the onset, at lower temperature, of a commensurate magnetic order similar to that existing in CeB6. However, unlike in the pure compound, an incommensurate magnetic order is formed at even higher temperature and persists in the antiferroquadrupolar phase down to the lock-in transition. These results are shown to reflect the interplay between various type of dipole exchange and higher multipole interactions in this series of compounds.