Combined neutron and x-ray diffraction experiments demonstrate the formation of a low-temperature minority tetragonal phase in Ba$_{0.76}$K$_{0.24}$Fe$_2$As$_2$ in addition to the majority magnetic, orthorhombic phase. A coincident enhancement in the
magnetic ($frac{1}{2}$ $frac{1}{2}$ 1) peaks shows that this minority phase is of the same type that was observed in Ba$_{1-x}$Na$_x$Fe$_2$As$_2$ ($0.24 leq x leq 0.28$), in which the magnetic moments reorient along the $c$-axis. This is evidence that the tetragonal magnetic phase is a universal feature of the hole-doped iron-based superconductors.
We present the evolution of the initial (up to ~ 10 kbar) hydrostatic, pressure dependencies of T_c and of the ambient pressure jump in the heat capacity associated with the superconducting transition as a function of Na - doping in the Ba(1-x)NaxFe2
As2 family of iron-based superconductors. For Na concentrations 0.15 <= x <= 0.9, the jump in specific heat at T_c, Delta C_p, follows the Delta C_p ~ T^3 scaling found for most BaFe2As2 - based superconductors. Pressure dependencies are non-monotonic for x = 0.2 and x = 0.24. For other Na concentrations T_c decreases under pressure in almost linear fashion. The anomalous behavior of the x = 0.2 and x = 0.24 samples under pressure are possibly due to the crossing of the phase boundaries of the narrow antiferromagnetic tetragonal phase, unique for the Ba(1-x)NaxFe2As2 series, with the application of pressure.
We report the results of a systematic investigation of the phase diagram of the iron-based superconductor, Ba1-xKxFe2As2, from x = 0 to x = 1.0 using high resolution neutron and x-ray diffraction and magnetization measurements. The polycrystalline sa
mples were prepared with an estimated compositional variation of Deltax <~ 0.01, allowing a more precise estimate of the phase boundaries than reported so far. At room temperature, Ba1-xKxFe2As2 crystallizes in a tetragonal structure with the space group symmetry of I4/mmm, but at low doping, the samples undergo a coincident first-order structural and magnetic phase transition to an orthorhombic (O) structure with space group Fmmm and a striped antiferromagnet (AF) with space group Fcmmm. The transition temperature falls from a maximum of 139K in the undoped compound to 0K at x = 0.252, with a critical exponent as a function of doping of 0.25(2) and 0.12(1) for the structural and magnetic order parameters, respectively. The onset of superconductivity occurs at a critical concentration of x = 0.130(3) and the superconducting transition temperature grows linearly with x until it crosses the AF/O phase boundary. Below this concentration, there is microscopic phase coexistence of the AF/O and superconducting order parameters, although a slight suppression of the AF/O order is evidence that the phases are competing. At higher doping, superconductivity has a maximum Tc of 38 K at x = 0.4 falling to 3 K at x = 1.0. We discuss reasons for the suppression of the spin-density-wave order and the electron-hole asymmetry in the phase diagram.