We study role of site substitutions at In and Te site in In2Te5 on the thermoelectric behavior. Single crystals with compositions In2(Te1-xSex)5 (x = 0, 0.05, 0.10) and Fe0.05In1.95(Te0.90Se0.10)5 were prepared using modified Bridgman-Stockbarger tec
hnique. Electrical and thermal transport properties of these single crystals were measured in the temperature range 6 - 395 K. A substantial decrease in thermal conductivity is observed in Fe substituted samples attributed to the enhanced phonon point-defect scattering. Marked enhancement in Seebeck coefficient S along with a concomitant suppression of electrical resistivity r{ho} is observed in Se substituted single crystals. An overall enhancement of thermoelectric figure of merit (zT) by a factor of 310 is observed in single crystals of Fe0.05In1.95(Te0.90Se0.10)5 compared to the parent In2Te5 single crystals.