نفذت الدراسة الحركية على التفاعل بين 2 - ميتيل 1,5 بنتان ثنائي أمين و الحمض الديميري الدسم C36 في الحالة المنصهرة، أنجز التفاعل عند الدرجات (ºC 164, 155, 140, 130, 113) و جرى تعيين قرينة الحموضة للمنتج. و قد وجد أن تفاعل الأميدة كان من المرتبة الثانية مع طاقة تنشيط mol g\j k (48.4.113, 130, 140, 155, 164 ºC حـرارة درجات عند (52, 57, 79, 80, 86)% تحول نسب حتى على الترتيب، ثـم يتحـول التفاعـل مـن المرتبـة الثانيـة إلـى المرتبـة الثالثـة بطاقـة تنـشيط .43.73k j/ g mol.
Kinetic studies were carried out on the reaction between 2-Methyl 1,5 diaminopentane and dimeric fatty acids in melt phase. The reaction was performed at 113, 130, 140, 155, and 164 ºC and followed by determining the acid value of the product .The polyamidation reaction was found to be of overall second order with an activation energy of 45.48 k cal⁄g mol up to (52, 57, 79, 80, 86)% conversion at (113, 130, 140, 155, 164) ºC and overall third order with an activation energy of 43.73 k cal⁄g mol above (52, 57, 79, 80, 86)% conversion at (113, 130, 140, 155, 164) ºC.
Artificial intelligence review:
Research summary
تتناول هذه الدراسة الحركية التفاعل بين 2-ميثيل 1,5 بنتان ثنائي أمين والحمض الديميري الدسم في الحالة المنصهرة. تم تنفيذ التفاعل عند درجات حرارة مختلفة (113، 130، 140، 155، 164 درجة مئوية) وتم تحديد قيمة الحموضة للمنتج. وُجد أن تفاعل الأميدة يتبع حركية من المرتبة الثانية حتى نسب تحول معينة (52، 57، 79، 80، 86%) مع طاقة تنشيط 45.48 كيلو جول/مول. بعد هذه النسب، يتحول التفاعل إلى مرتبة ثالثة مع طاقة تنشيط 43.73 كيلو جول/مول. تم حساب درجة البلمرة، معدل الوزن الجزيئي العددي، ومعدل الوزن الجزيئي الوزني خلال أزمنة مختلفة، ولوحظ أن العلاقة بين هذه القيم والزمن هي علاقة خطية حتى نسب التحول المذكورة. النتائج تتفق مع الدراسات السابقة لتفاعلات البولي أميدات الأخرى، وتم الوصول إلى معدل وزن جزيئي عددي 9572.536 ومعدل وزن جزيئي وزني 18494.86 عند درجة حرارة 164 درجة مئوية.
Critical review
تُعد هذه الدراسة إضافة قيمة لفهم حركية تفاعل الأميدات في الحالة المنصهرة، ولكن هناك بعض النقاط التي يمكن تحسينها. أولاً، لم يتم توضيح تأثير العوامل البيئية مثل الرطوبة والضغط على التفاعل، مما قد يؤثر على النتائج. ثانياً، كان من الممكن توسيع نطاق درجات الحرارة المدروسة للحصول على صورة أكثر شمولية عن التفاعل. ثالثاً، لم يتم مناقشة التطبيقات العملية للنتائج بشكل كافٍ، مما يجعل من الصعب تقييم الفائدة العملية لهذه الدراسة. على الرغم من هذه النقاط، فإن الدراسة توفر معلومات قيمة عن حركية تفاعل الأميدات وتفتح الباب لمزيد من الأبحاث في هذا المجال.
Questions related to the research
-
ما هي درجات الحرارة التي تم تنفيذ التفاعل عندها؟
تم تنفيذ التفاعل عند درجات حرارة 113، 130، 140، 155، و164 درجة مئوية.
-
ما هي طاقة التنشيط لتفاعل الأميدة من المرتبة الثانية؟
طاقة التنشيط لتفاعل الأميدة من المرتبة الثانية هي 45.48 كيلو جول/مول.
-
كيف تتغير مرتبة التفاعل بعد نسب التحول المعينة؟
بعد نسب التحول المعينة (52، 57، 79، 80، 86%)، يتحول التفاعل من مرتبة ثانية إلى مرتبة ثالثة.
-
ما هي العلاقة بين معدل الوزن الجزيئي العددي والزمن؟
العلاقة بين معدل الوزن الجزيئي العددي والزمن هي علاقة خطية حتى نسب التحول المذكورة.
References used
Brydson, J. A. (1999). Plastics Materials, University of North London, 7 th ed, p. 478- 480
Vedanayagam, H. S. Kale, V. Subbarao, R. (1992). Kinetics of reaction of C36 dimeric fatty acids and ethylenediamine in solution, J. Appl. Polym. Sci.V. 45, P.2245-2248
Heidarian, J. Ghasem, N. M. Daud, W. (2003). Kinetic model for polymerization 0f dimer fatty acids with ethylenediamine, University of Malaya, F. 0135, p. 45
rate research
Read More
Kinetic studies were carried out on the reaction between dimeric fatty acid
C36 with 1.3 Diamino propane and 1.4 Diamino butane and 1.6 Diamino hexane
and 1.8 Diamino octane in molten phase. The reaction was performed at 145ºC.
The polyamidation r
eaction was found to be on the overall a second order up to
83% conversion for reaction dimeric fatty acid C36 with 1.3 Diamino propane
and 86% conversion for reaction dimeric fatty acid C36 with 1.4 Diamino
butane and 87% conversion for reaction dimeric fatty acid C36 with 1.6
Diamino hexane and 1.8 Diamino octane then the reaction order changes to the
third order above last conversion. The degree of polymerization,number
average molecular weight and weight average molecular weight have been
calculated during different times. Their relationships with the times are linear
until last conversion. The melting point and thermodynamic constants for
melting are determined by use of differential scanning calorimetry DSC. The
melting point and thermodynamic constants increase by increasing the length
of reacted amine series.
Fattypolyamide was prepared by reaction of (1,5-Diamino pentane) with
dimeric fatty acid C36 in molten state. The reaction was performed at 110 C˚
without catalyst, then with (Phosphoric acid, Sulphoric acid and Manganese
dioxides). The Kinetic st
udy was carried out on the reaction and followed by
determining the acid value of the product. The polyamidation reaction was
found to be on the overall a second order up to 59% conversion. Then the
reaction order changes. We found that the Catalyst increases the velocity of the
reaction with manganese dioxides the best Catalyst. The Degree of
Polymerization, Number Average Molecular Weight and Weight Average
Molecular Weight have been calculated during different times. The
relationships between Degree of Polymerization and Number Average
Molecular Weight, Weight Average Molecular Weight with times are linear
until 59%conversion at 110˚C with used catalysts. The highest (N.A.M.W) and
(W.A.M.W) was accomplished with the Catalyst MnO2.
Kinetic studies were carried out on the reaction between 1,10–
Decanedioland dimeric fatty acid C36 in melt phase. The reaction was
performed at 140, 150, 160, 170, and 185ºC and followed by determining the
acid value of the product.
Kinetic studies were carried out on the reaction between ′4,4-Methylenebis
(2-methylcyclohexylamine) and dimeric fatty acid C36 in molten state by using
a catalyst of sulpheric acid compared with the same kinetic of reaction without
catalyst.
The
reaction was performed at 150, and 160 ˚C and followed by determining
the acid value of the product.The polyamidation reaction was found to be of
overall a second order until equilibrium state. Moreover, the catalyst increases
speed of the reaction. Polyamidation reaction was automatic whereas the value
of free energy was negative and the reaction was endothermic, and this is
shown in change of positive enthalpy values.
Study the kinetics degradation of poly (dimeric acid C36 with 1.9 – diamino
nonane) was carried out by thermal analysis (TGA), and thermodynamic and
equilibrium constants have been defined, moreover, study the kinetics of
reaction between 1.9 – di
amino nonane and dimer fatty acid C36 was carried
out in molten state, the reaction was performed at 160 ºC, the acid value, and
percentage of carboxylic functions of the product were determined. The
polyamidation reaction was found to be of overall second order until
conversion of 97% at 160 ºC, then the order of reaction changes.
حركية تفاعل الأميدة
Kinetic of polyamidation reaction
Number Average Molecular Weight
Weight Average Molecular Weight
الحمض الديميري الدسم C36
ثنائيات الأمين
ثوابت ترموديناميكية
الوزن الجزيئي الوسطي العددي
الوزن الجزيئي الوسطي الوزني
الوزن الجزيئي الوسطي اللزوجي
Dimeric fatty acid C36
Diamines
Thermodynamic constants
Viscosity molecular weight
المزيد..
Log in to be able to interact and post comments
comments
Fetching comments
Sign in to be able to follow your search criteria