Register a new userInfluence of pulsed laser deposition growth conditions on the thermoelectric properties of Ca3Co4O9 thin films
373
0
0.0
(
0
)
Ask ChatGPT about the research
No Arabic abstract
Thin films of the misfit cobaltite Ca3Co4O9 were grown on (0001)-oriented (c-cut) sapphire substrates, using the pulsed-laser deposition techniques. The dependence of the thermoelectric/transport properties on the film growth conditions was investigated
rate research
Read More
Recently, nanolaminated ternary carbides have attracted immense interest due to the concomitant presence of both ceramic and metallic properties. Here, we grow nanolaminate Ti3AlC2 thin films by pulsed laser deposition on c-axis-oriented sapphire substrates and, surprisingly, the films are found to be highly oriented along the (103) axis normal to the film plane, rather than the (000l) orientation. Multiple characterization techniques are employed to explore the structural and chemical quality of these films, the electrical and optical properties, and the device functionalities. The 80-nm thick Ti3AlC2 film is highly conducting at room temperature (resistivity of 50 micro ohm-cm), and a very-low-temperature coefficient of resistivity. The ultrathin (2 nm) Ti3AlC2 film has fairly good optical transparency and high conductivity at room temperature (sheet resistance of 735 ohm). Scanning tunneling microscopy reveals the metallic characteristics (with finite density of states at the Fermi level) at room temperature. The metal-semiconductor junction of the p-type Ti3AlC2 film and n-Si show the expected rectification (diode) characteristics, in contrast to the ohmic contact behavior in the case of Ti3AlC2 on p-Si. A triboelectric-nanogenerator-based touch-sensing device, comprising of the Ti3AlC2 film, shows a very impressive peak-to-peak open-circuit output voltage of 80 V. These observations reveal that pulsed laser deposited Ti3AlC2 thin films have excellent potential for applications in multiple domains, such as bottom electrodes, resistors for high-precision measurements, Schottky diodes, ohmic contacts, fairly transparent ultrathin conductors, and next-generation biomechanical touch sensors for energy harvesting.
The crystal structures of LaAlO3 films grown by pulsed laser deposition on SrTiO3 substrates at oxygen pressure of 10-3 mbar or 10-5 mbar, where kinetics of ablated species hardly depend on oxygen background pressure, are compared. Our results show that the interface between LaAlO3 and SrTiO3 is sharper when the oxygen pressure is lower. Over time, the formation of various crystalline phases is observed while the crystalline thickness of the LaAlO3 layer remains unchanged. X-ray scattering as well as atomic force microscopy measurements indicate three-dimensional growth of such phases, which appear to be fed from an amorphous capping layer present in as-grown samples.
Epitaxial titanium diboride thin films have been deposited on sapphire substrates by Pulsed Laser Ablation technique. Structural properties of the films have been studied during the growth by Reflection High Energy Electron Diffraction (RHEED) and ex-situ by means of X-ray diffraction techniques; both kinds of measurements indicate a good crystallographic orientation of the TiB2 film both in plane and along the c axis. A flat surface has been observed by Atomic Force Microscopy imaging. Electrical resistivity at room temperature resulted to be five times higher than the value reported for single crystals. The films resulted to be also very stable at high temperature, which is very promising for using this material as a buffer layer in the growth of magnesium diboride thin films.
Possible existence of topologically protected surface in samarium hexaboride has created a strong need for investigations allowing to distinguish between properties coming from the surface states and those originating in the (remaining) bulk. Studies of SmB6 thin films represent a favorable approach allowing well defined variations of the bulk volume that is not affected by surface states. Moreover, thin films are highly desirable for potential technology applications. However, the growth of SmB6 thin films is accompanied by technology problems, which are typically associated with maintaining the correct stoichiometry of samarium and boron. Here we present feasibility study of SmB6 thin film synthesis by pulsed laser deposition (PLD) from a single stoichiometric SmB6 target. As proved by Rutherford Backscattering Spectrometry (RBS), we succeeded to obtain the same ratio of samarium and boron in the films as that in the target. Thin films revealing characteristic electrical properties of (crystalline) SmB6 were successfully deposited on MgO, sapphire, and glass-ceramics substrates, when the substrates were kept at temperature of 600$^circ$ C during the deposition. Performed electrical resistance studies have revealed that bulk properties of the films are only slightly affected by the substrate. Our results indicate that PLD is a suitable method for complex and intensive research of SmB6 and similar systems.
Pulsed laser deposition, a non-equilibrium thin-film growth technique, was used to stabilize metastable tetragonal iron sulfide (FeS), the bulk state of which is known as a superconductor with a critical temperature of 4 K. Comprehensive experiments revealed four important factors to stabilize tetragonal FeS epitaxial thin films: (i) an optimum growth temperature of 300 {deg}C followed by thermal quenching, (ii) an optimum growth rate of ~7 nm/min, (iii) use of a high-purity bulk target, and (iv) use of a single-crystal substrate with small in-plane lattice mismatch (CaF2). Electrical resistivity measurements indicated that none of all the films exhibited superconductivity. Although an electric double-layer transistor structure was fabricated using the tetragonal FeS epitaxial film as a channel layer to achieve high-density carrier doping, no phase transition was observed. Possible reasons for the lack of superconductivity include lattice strain, off-stoichiometry of the film, electrochemical etching by the ionic liquid under gate bias, and surface degradation during device fabrication.