No Arabic abstract
Recently, based on the phase-field modeling, it was predicted that Hf1-xZrxO2 (HZO) exhibits the morphotropic phase boundary (MPB) in its compositional phase diagram. Here, we investigate the effect of structural changes between tetragonal (t) and orthorhombic (o) phases on the ferroelectric and dielectric properties of HZO films to probe the existence of MPB region. The structural analysis show that by adjusting the ozone dosage during the atomic layer deposition process and annealing conditions, different ratios of t- to o-phases (f_(t/o) ) were achieved which consequently affect the ferroelectric and dielectric properties of the samples. Polarization versus electric field measurements show a remarkable increase in ferroelectric characteristics (Pr and Ec) of the sample that contains the minimum t-phase fraction (f_(t/o)~ 0.04). This sample shows the lowest dielectric constant compared to the other samples which is due to the formation of ferroelectric o-phase. The sample that contains the maximum f_(t/o)~ 0.41 demonstrates the highest dielectric response. By adjusting the f_(t/o), a large dielectric constant of ~ 55 is achieved. Our study reveals a direct relation between f_(t/o) and dielectric constant of HZO thin films which can be understood by considering the density of MPB region.
We report on the discovery of a lead-free morphotropic phase boundary in Sm doped BiFeO3 with a simple perovskite structure using the combinatorial thin film strategy. The boundary is a rhombohedral to pseudo-orthorhombic structural transition which exhibits a ferroelectric (FE) to antiferroelectric (AFE) transition at approximately Bi0.86Sm0.14FeO3 with dielectric constant and out-of-plane piezoelectric coefficient comparable to those of epitaxial (001) oriented Pb(Zr,Ti)O3 (PZT) thin films at the MPB. The discovered composition may be a strong candidate of a Pb-free piezoelectric replacement of PZT.
After decades of searching for robust nanoscale ferroelectricity that could enable integration into the next generation memory and logic devices, hafnia-based thin films have appeared as the ultimate candidate because their ferroelectric (FE) polarization becomes more robust as the size is reduced. This exposes a new kind of ferroelectricity, whose mechanism still needs to be understood. Towards this end, thin films with increased crystal quality are needed. We report the epitaxial growth of Hf0.5Zr0.5O2 (HZO) thin films on (001)-oriented La0.7Sr0.3MnO3/SrTiO3 (STO) substrates. The films, which are under epitaxial compressive strain and are predominantly (111)-oriented, display large FE polarization values up to 34 {mu}C/cm2 and do not need wake-up cycling. Structural characterization reveals a rhombohedral phase, different from the commonly reported polar orthorhombic phase. This unexpected finding allows us to propose a compelling model for the formation of the FE phase. In addition, these results point towards nanoparticles of simple oxides as a vastly unexplored class of nanoscale ferroelectrics.
We investigate the microstructural evolution in a ferroelectric to antiferroelectric phase transition at the morphotropic phase boundary in the Bi(1-x)SmxFeO3 system. Continuous Sm3+ substitution on the A-site induces short-range anti-parallel cation displacements as verified by the appearance of localized 1/4(110) weak spots in selected area electron diffraction patterns for 0.1<x<0.14 samples, and thus onset of antiferroelectricity. Kinetic Monte Carlo simulations confirm that increasing the strength of the anti-parallel interactions (i.e. increasing x) induces a ferroelectric to antiferroelectric transition. For 0.14<x<0.2 antiphase oxygen octahedra tilts induce complete antiferroelectricity.
Doping ferroelectric Hf0.5Zr0.5O2 with La is a promising route to improve endurance. However, the beneficial effect of La on the endurance of polycrystalline films may be accompanied by degradation of the retention. We have investigated the endurance - retention dilemma in La-doped epitaxial films. Compared to undoped epitaxial films, large values of polarization are obtained in a wider thickness range, whereas the coercive fields are similar, and the leakage current is substantially reduced. Compared to polycrystalline La-doped films, epitaxial La-doped films show more fatigue but there is not significant wake-up effect and endurance-retention dilemma. The persistent wake-up effect common to polycrystalline La-doped Hf0.5Zr0.5O2 films, is limited to a few cycles in epitaxial films. Despite fatigue, endurance in epitaxial La-doped films is more than 1010 cycles, and this good property is accompanied by excellent retention of more than 10 years. These results demonstrate that wake-up effect and endurance-retention dilemma are not intrinsic in La-doped Hf0.5Zr0.5O2.
The metastable orthorhombic phase of hafnia is generally obtained in polycrystalline films, whereas in epitaxial films, its formation has been much less investigated. We have grown Hf0.5Zr0.5O2 films by pulsed laser deposition, and the growth window (temperature and oxygen pressure during deposition and film thickness) for epitaxial stabilization of the ferroelectric phase is mapped. The remnant ferroelectric polarization, up to around 24 uC/cm2, depends on the amount of orthorhombic phase and interplanar spacing and increases with temperature and pressure for a fixed film thickness. The leakage current decreases with an increase in thickness or temperature, or when decreasing oxygen pressure. The coercive electric field (EC) depends on thickness (t) according to the coercive electric field (Ec) - thickness (t)-2/3 scaling, which is observed for the first time in ferroelectric hafnia, and the scaling extends to thicknesses down to around 5 nm. The proven ability to tailor the functional properties of high-quality epitaxial ferroelectric Hf0.5Zr0.5O2 films paves the way toward understanding their ferroelectric properties and prototyping devices.