To explore the origin of the unusual non-bulk superconductivity with a Tc up to 49 K reported in the rare-earth-doped CaFe2As2 , the chemical composition, magnetization, specific heat, resistivity, and annealing effect are systematically investigated on nominal (Ca1-xRx)Fe2As2 single crystals with different xs and R = La, Ce, Pr, and Nd. All display a doping-independent Tc once superconductivity is induced, a doping-dependent low field superconducting volume fraction f, and a large magnetic anisotropy {eta} in the superconducting state, suggesting a rather inhomogeneous superconducting state in an otherwise microscale-homogenous superconductor. The wavelength dispersive spectroscopy and specific heat show the presence of defects which are closely related to f, regardless of the R involved. The magnetism further reveals that the defects are mainly superparamagnetic clusters for R = Ce, Pr, and Nd with strong intercluster interactions, implying that defects are locally self-organized. Annealing at 500 {deg}C, without varying the doping level x, suppresses f profoundly but not the Tc. The above observations provide evidence for the crucial role of defects in the occurrence of the unusually high Tc ~ 49 K in (Ca1-xRx)Fe2As2 and are consistent with the interface-enhanced superconductivity recently proposed.
rate research
Read More
A new hight Tc Fe-based compound system, AFe2As2 with A = K, Cs, K/Sr and Cs/Sr has been found. Through electron-doping, Tc of the A = K and Cs compounds rises to ~37 K, and finally enter a spin-density-wave state (SDW) through further electron doping with Sr. The observation demonstrates the crucial role of the (FeAs)-layers in the superconductivity in the Fe-based layered system and the special feature of elemental A-layers in this complex chemical system may provide new avenues to superconductivity at a higher Tc.
Single crystalline CaFe2As2 and (Ca1-xNax)Fe2As2 polycrystals (0 < x < 0.66) are synthesized and characterized using structural, magnetic, electronic transport, and heat capacity measurements. These measurements show that the structural/magnetic phas
e transition in CaFe2As2 at 165 K is monotonically suppressed by the Na doping and that superconductivity can be realized over a wide doping region. For 0.3 < x < 0.36, the magnetic susceptibilities indicate the possible coexistence of the spin density wave (SDW) and superconductivity. Superconducting phases corresponding to the Na doping level in (Ca1-xNax)Fe2As2 for nominal x = 0.36, 0.4, 0.5, 0.6, and 0.66, with Tc = 17 K, 19 K, 22 K, 33 K, and 33 K, respectively, are identified. The effects of the magnetic field on the superconductivity transitions for x = 0.66 samples with high upper critical fields Hc2 approx 103 T are studied, and a phase diagram of the SDW and superconductivity as a function of the doping level is thus presented.
Following the discovery of superconductivity in an iron-based arsenide LaO1-xFxFeAs with a superconducting transition temperature (Tc) of 26 K[1], Tc was pushed up surprisingly to above 40 K by either applying pressure[2] or replacing La with Sm[3], Ce[4], Nd[5] and Pr[6]. The maximum Tc has climbed to 55 K, observed in SmO1-xFxFeAs[7, 8] and SmFeAsO1-x[9]. The value of Tc was found to increase with decreasing lattice parameters in LnFeAsO1-xFx (Ln stands for the lanthanide elements) at an apparently optimal doping level. However, the F- doping in GdFeAsO is particularly difficult[10,11] due to the lattice mismatch between the Gd2O2 layers and Fe2As2 layers. Here we report observation of superconductivity with Tc as high as 56 K by the Th4+ substitution for Gd3+ in GdFeAsO. The incorporation of relatively large Th4+ ions relaxes the lattice mismatch, hence induces the high temperature superconductivity.
Far and mid infrared optical pulses have been shown to induce non-equilibrium unconventional orders in complex materials, including photo-induced ferroelectricity in quantum paraelectrics, magnetic polarization in antiferromagnets and transient superconducting correlations in the normal state of cuprates and organic conductors. In the case of non-equilibrium superconductivity, femtosecond drives have generally resulted in electronic properties that disappear immediately after excitation, evidencing a state that lacks intrinsic rigidity. Here, we make use of a new optical device to drive metallic K$_3$C$_{60}$ with mid-infrared pulses of tunable duration, ranging between one picosecond and one nanosecond. The same superconducting-like optical properties observed over short time windows for femtosecond excitation are shown here to become metastable under sustained optical driving, with lifetimes in excess of ten nanoseconds. Direct electrical probing becomes possible at these timescales, yielding a vanishingly small resistance. Such a colossal positive photo-conductivity is highly unusual for a metal and, when taken together with the transient optical conductivities, it is rather suggestive of metastable light-induced superconductivity.
Polycrystalline sample FeSe was synthesized by a self-flux solution method which shows a zero resistance temperature up to 10.9 K and a Tconset (90% rhon, rhon: normal state resistivity) up to 13.3 K. The decrease of superconducting transition temperature by heat treatment indicates that internal crystallographic strain which plays the same effect as external pressure is the origin of its high Tc. The fluctuation conductivity was studied which could be well described by 3D Aslamazov-Larkin (AL) power law. The estimated value of coherence length xic=9.2 AA is larger than the distance between conducting layers (~6.0 AA), indicating the three-dimensional nature of superconductivity in this compound.