Register a new userThree Dimensional Superconductivity in FeSe with Tczero Up to 10.9 K Induced by Internal Strain
133
0
0.0
(
0
)
Ask ChatGPT about the research
No Arabic abstract
Polycrystalline sample FeSe was synthesized by a self-flux solution method which shows a zero resistance temperature up to 10.9 K and a Tconset (90% rhon, rhon: normal state resistivity) up to 13.3 K. The decrease of superconducting transition temperature by heat treatment indicates that internal crystallographic strain which plays the same effect as external pressure is the origin of its high Tc. The fluctuation conductivity was studied which could be well described by 3D Aslamazov-Larkin (AL) power law. The estimated value of coherence length xic=9.2 AA is larger than the distance between conducting layers (~6.0 AA), indicating the three-dimensional nature of superconductivity in this compound.
rate research
Read More
Following the discovery of superconductivity in an iron-based arsenide LaO1-xFxFeAs with a superconducting transition temperature (Tc) of 26 K[1], Tc was pushed up surprisingly to above 40 K by either applying pressure[2] or replacing La with Sm[3], Ce[4], Nd[5] and Pr[6]. The maximum Tc has climbed to 55 K, observed in SmO1-xFxFeAs[7, 8] and SmFeAsO1-x[9]. The value of Tc was found to increase with decreasing lattice parameters in LnFeAsO1-xFx (Ln stands for the lanthanide elements) at an apparently optimal doping level. However, the F- doping in GdFeAsO is particularly difficult[10,11] due to the lattice mismatch between the Gd2O2 layers and Fe2As2 layers. Here we report observation of superconductivity with Tc as high as 56 K by the Th4+ substitution for Gd3+ in GdFeAsO. The incorporation of relatively large Th4+ ions relaxes the lattice mismatch, hence induces the high temperature superconductivity.
To explore the origin of the unusual non-bulk superconductivity with a Tc up to 49 K reported in the rare-earth-doped CaFe2As2 , the chemical composition, magnetization, specific heat, resistivity, and annealing effect are systematically investigated on nominal (Ca1-xRx)Fe2As2 single crystals with different xs and R = La, Ce, Pr, and Nd. All display a doping-independent Tc once superconductivity is induced, a doping-dependent low field superconducting volume fraction f, and a large magnetic anisotropy {eta} in the superconducting state, suggesting a rather inhomogeneous superconducting state in an otherwise microscale-homogenous superconductor. The wavelength dispersive spectroscopy and specific heat show the presence of defects which are closely related to f, regardless of the R involved. The magnetism further reveals that the defects are mainly superparamagnetic clusters for R = Ce, Pr, and Nd with strong intercluster interactions, implying that defects are locally self-organized. Annealing at 500 {deg}C, without varying the doping level x, suppresses f profoundly but not the Tc. The above observations provide evidence for the crucial role of defects in the occurrence of the unusually high Tc ~ 49 K in (Ca1-xRx)Fe2As2 and are consistent with the interface-enhanced superconductivity recently proposed.
We report here that a new superconducting phase with much higher Tc has been found in K intercalated FeSe compound with excess Fe. We successfully grew crystals by precisely controlling the starting amount of Fe. Besides the superconducting (SC) transition at ~30 K, we observed a sharp drop in resistivity and a kink in susceptibility at 44 K. By combining thermodynamic measurements with electron spin resonance (ESR), we demonstrate that this is a new SC transition. Structural analysis unambiguously reveals two phases coexisting in the crystals, which are responsible respectively for the SC transitions at 30 and 44 K. The structural experiments and first-principles calculations consistently indicate that the 44 K SC phase is close to a 122 structure, but with an unexpectedly large c-axis of 18.10 {AA}. We further find a novel monotonic dependence of the maximum Tc on the separation of neighbouring FeSe layers.
A new hight Tc Fe-based compound system, AFe2As2 with A = K, Cs, K/Sr and Cs/Sr has been found. Through electron-doping, Tc of the A = K and Cs compounds rises to ~37 K, and finally enter a spin-density-wave state (SDW) through further electron doping with Sr. The observation demonstrates the crucial role of the (FeAs)-layers in the superconductivity in the Fe-based layered system and the special feature of elemental A-layers in this complex chemical system may provide new avenues to superconductivity at a higher Tc.
We have studied the effect of tensile strain on the superconductivity in FeSe films. 50 nm, 100 nm, and 200 nm FeSe films were grown on MgO, SrTiO$_3$, and LaAlO$_3$ substrates by using a pulsed laser deposition technique. X-ray diffraction analysis showed that the tetragonal phase is dominant in all of our FeSe films. The 50 nm FeSe films on MgO and SrTiO$_3$ are under tensile strain, while the 50 nm FeSe film on LaAlO$_3$ and the other thick FeSe films are unstrained. Superconducting transitions have been observed in unstrained FeSe films with T$_{onset}$ $approx$ 8 K, which is close to the bulk value. However, no sign of superconductivity has been observed in FeSe films under tensile strain down to 5 K. There is evidence to show that tensile strain suppresses superconductivity in FeSe films.