With the motivation of discovering high-temperature superconductors, evolutionary algorithm is employed to search for all stable compounds in the Sn-H system. In addition to the traditional SnH$_4$, new hydrides SnH$_8$, SnH$_{12}$ and SnH$_{14}$ are found to be thermodynamically stable at high pressure. Dynamical stability and superconductivity of tin-hydrides are systematically investigated. I$bar{4}$m2-SnH$_8$, C2/m-SnH$_{12}$ and C2/m-SnH$_{14}$ exhibit higher superconducting transition temperatures of 81, 93 and 97 K compared to the traditional compound SnH$_4$ with T$_c$ of 52 K at 200 GPa. An interesting bent H$_3^-$ in I$bar{4}$m2-SnH$_8$ and novel liner H$_4^-$ in C2/m-SnH$_{12}$ are observed. All the new tin-hydrides remain metallic over their predicted range of stability. The intermediate-frequency wagging and bending vibrations have more contribution to electron-phonon coupling parameter than high-frequency stretching vibrations of H$_2$ and H$_3$.
rate research
Read More
The long-sought goal of room-temperature superconductivity has reportedly recently been realized in a carbonaceous sulfur hydride compound under high pressure, as reported by Snider et al. [1]. The evidence presented in that paper is stronger than in other similar recent reports of high temperature superconductivity in hydrides under high pressure [2-7], and has been received with universal acclaim [8-10]. Here we point out that features of the experimental data shown in Ref. [1] indicate that the phenomenon observed in that material is not superconductivity. This observation calls into question earlier similar claims of high temperature conventional superconductivity in hydrides under high pressure based on similar or weaker evidence [2-7].
The discovery of high-temperature conventional superconductivity in H3S with a critical temperature of Tc=203 K was followed by the recent record of Tc ~250 K in the face-centered cubic (fcc) lanthanum hydride LaH10 compound. It was realized in a new class of hydrogen-dominated compounds having a clathrate-like crystal structure in which hydrogen atoms form a 3D framework and surround a host atom of rare earth elements. Yttrium hydrides are predicted to have even higher Tc exceeding room temperature. In this paper, we synthesized and refined the crystal structure of new hydrides: YH4, YH6, and YH9 at pressures up to 237 GPa finding that YH4 crystalizes in the I4/mmm lattice, YH6 in Im-3m lattice and YH9 in P63/mmc lattice in excellent agreement with the calculations. The observed very high-temperature superconductivity is comparable to that found in fcc-LaH10: the pressure dependence of Tc for YH9 also displays a dome like shape with the highest Tc of 243 K at 201 GPa. We also observed a Tc of 227 K at 237 GPa for the YH6 phase. However, the measured Tcs are notably lower by ~30 K than predicted. Evidence for superconductivity includes the observation of zero electrical resistance, a decrease of Tc under an external magnetic field and an isotope effect. The theoretically predicted fcc YH10 with the promising highest Tc>300 K was not stabilized in our experiments under pressures up to 237 GPa.
Various tin hydrides SnHx (x = 4, 8, 12, 14) have been theoretically predicted to be stable at high pressures and to show high-critical-temperature superconductivity with Tc ranging from about 70 to 100 K. However, experimental verifications for any of these phases are still lacking to date. Here, we report on the in-situ synthesis, electrical resistance, and synchrotron x-ray diffraction measurements of SnHx at ~ 200 GPa. The main phase of the obtained sample can be indexed with the monoclinic C2/m SnH12 via comparison with the theoretical structural modes. A sudden drop of resistance and the systematic downward shift under external magnetic fields signals the occurrence of superconductivity in SnHx at Tc = ~ 70 K with an upper critical field u0Hc2(0) = ~ 11.2 T, which is relatively low in comparison with other reported high-Tc superhydrides. Various characteristic superconducting parameters are estimated based on the BCS theory.
Motivated by the recent claim of hot superconductivity with critical temperatures up to 550 K in La + x hydrides (arXiv:2006.03004), we investigate the high-pressure phase diagram of possible compounds that may have formed in the experiment, using first-principles calculations for evolutionary crystal structure prediction and superconductivity. Starting from the hypothesis that the observed T$_c$ may be realized by successive heating upon a pre-formed LaH$_{10}$ phase, we examine plausible ternaries of lanthanum, hydrogen and other elements present in the diamond anvil cell: boron, nitrogen, carbon, platinum, gallium, gold. We find that only boron forms superhydride-like structures that can host high-Tc superconductivity, but the predicted Tc are incompatibe with the experimental reports. Our results indicate that, while the claims of hot superconductivity should be reconsidered, it is very likely that unkwown H-rich ternary or multinary phases containing lanthanum, boron and hydrogen may have formed under the reported experimental conditions, and that these may exhibit superconducting properties comparable, or even superior, to those of currently known hydrides.
The recent discovery of superconductivity at 190~K in highly compressed H$_{2}$S is spectacular not only because it sets a record high critical temperature, but because it does so in a material that appears to be, and we argue here that it is, a conventional strong-coupling BCS superconductor. Intriguingly, superconductivity in the observed pressure and temperature range was predicted theoretically in a similar compound H$_{3}$S. Several important questions about this remarkable result, however, are left unanswered: (1) Does the stoichiometry of the superconducting compound differ from the nominal composition, and could it be the predicted H$_{3}$S compound? (2) Is the physical origin of the anomalously high critical temperature related only to the high H phonon frequencies, or does strong electron-ion coupling play a role? We show that at experimentally relevant pressures H$_2$S is unstable, decomposing into H$_3$S and S, and that H$_3$S has a record high $T_c$ due to its covalent bonds driven metallic. The main reason for this extraordinarily high $T_c$ in H$_3$S as compared with MgB$_2$, another compound with a similar superconductivity mechanism, is the high vibrational frequency of the much lighter H atoms.
Log in to be able to interact and post comments
comments
Fetching comments
Sign in to be able to follow your search criteria