The alloys of non-centrosymmetric superconductor, Re$_3$W, which were reported to have an $alpha$-Mn structure [P. Greenfield and P. A. Beck, J. Metals, N. Y. textbf{8}, 265 (1959)] with $T_mathrm{c}=9 $K were prepared by arc melting. The ac susceptibility and low-temperature specific heat were measured on these alloys. It is found that there are two superconducting phases coexisting in the samples with $T_mathrm{c1}sim9 $K and $T_mathrm{c2}sim7 $K, both of which have a non-centrosymmetric structure as reported previously. By analyzing the specific heat data measured in various magnetic fields, we found that the absence of the inversion symmetry does not lead to the deviation from a s-wave pairing symmetry in Re$_3$W.
rate research
Read More
We report on the magnetic and superconducting properties of LaO0.5F0.5BiS2 by means of zero- (ZF) and transverse-field (TF) muon-spin spectroscopy measurements (uSR). Contrary to previous results on iron-based superconductors, measurements in zero field demonstrate the absence of magnetically ordered phases. TF-uSR data give access to the superfluid density, which shows a marked 2D character with a dominant s-wave temperature behavior. The field dependence of the magnetic penetration depth confirms this finding and further suggests the presence of an anisotropic superconducting gap.
We have investigated the superconducting state of the non-centrosymmetric compound Re6Zr using magnetization, heat capacity, and muon-spin relaxation/rotation (muSR) measurements. Re6Zr has a superconducting transition temperature, Tc = 6.75 K. Transverse-field muSR experiments, used to probe the superfluid density, suggest an s-wave character for the superconducting gap. However, zero and longitudinal-field muSR data reveal the presence of spontaneous static magnetic fields below Tc indicating that time-reversal symmetry is broken in the superconducting state and an unconventional pairing mechanism. An analysis of the pairing symmetries identifies the ground states compatible with time-reversal symmetry breaking.
We report specific heat capacity measurements on a LiFeAs single crystal at temperatures down to 400 mK and magnetic fields up to 9 Tesla. A small specific heat jump at Tc and finite residual density of states at T=0 K in the superconducting (SC) state indicate that there are strong unitary scatterers that lead to states within the SC gap. A sub-linear magnetic field dependence of the Sommerfeld coefficient gamma(H) at T=0 K is equally well fitted by both a nodal d-wave gap as well as a sign changing multiband pm s-wave gap. When impurity effects are taken into account, however, the linear temperature dependence of the electronic specific heat C_{el}/T at low temperatures argues against a nodal d-wave superconducting gap. We conclude that the SC state of LiFeAs is most compatible with the multiband pm s-wave SC state with the gap values Delta_{small}=0.46 Delta_{large}.
We report measurements of the temperature dependence of the magnetic penetration depth lambda(T) in non-centrosymmetric superconductor Re_3W. We employed two experimental techniques: extraction of lambda(T) from magnetic {em dc}-susceptibility, measured on a powder sample, and the rf tunnel diode resonator technique, where a bulk polycrystalline sample was used. The results of both techniques agree: the temperature dependence of the penetration depth can be well described by weak-coupling, dirty-limit, s-wave BCS theory where we obtain $Delta(0)/k_BT_C=1.76$. No evidence for unconventional pairing resulting from the absence of the inversion symmetry is found.
A high quality superconducting Li$_{0.68}$NbO$_2$ polycrystalline sample was synthesized by deintercalation of Li ions from Li$_{0.93}$NbO$_2$. The field dependent resistivity and specific heat were measured down to 0.5 K. The upper critical field $H_{c2} (T)$ is deduced from the resistivity data and $H_{c2}(0)$ is estimated to be $sim 2.98$ T. A notable specific heat jump is observed at the superconducting transition temperature $T_c sim 5.0$ K at zero field. Below $T_c$, the electronic specific heat shows a thermal activated behavior and agrees well with the theoretical result of the BCS s-wave superconductors. It indicates that the superconducting pairing in Li$_{0.68}$NbO$_2$ has s-wave symmetry.