The Objective is to determined whether enamel conditioning with sodium
hypochlorite (5,25%) and EDTA prior to etching was increased shear
bond strength of orthodontic brackets bonded with resin – modified glass
ionomer. our sample consisted of 42 extracted human premolars were
randomly divided into 3 groups.
The aim of this study To compare in vitro shear bond strength (SBS) of different
orthodontic adhesives in and rebonding metal brackets after preparing their bases
mechanically.
Material and methods:Sample consisted of 40 extracted first premolars,
randomly
divided into two groups (n=20),.Adhesive removed by tungsten carbide bur later the
brackets were rebonded. The tests were performed in a tecnotest (6kN) SBS testing
machine, at a speed of 1 mm/min.
It was found that the mean shear bond strength of Reseliencewas 19.25 MPa and that
of Heliosit orthodontic was 10.25MPa.We foundthat the mean shear bond strength of
rebonding forReselience was 13.70 and 7.95 forHeliosit.The t-test revealed that there was a
significant difference between the shear bond strength of the two groups.
We found a significant difference between bonding and rebondingfor
Reselience,while there was no significant difference between bonding and rebonding for
Heliosit.
The Purpose of this study was to evaluate and compare the shear bond strength
(SBS) of two composite repair systems to zirconia-ceramic with and without sandblasting.
This study aims to evaluate zirconia bond strength bonded with resin cement
after deferent surface treatments.