Three samples of alumina_zirconia mixed oxid AL2O3_Zr2O4(1;0.25;0.1) mole ratio
based on oxides were prepared by sol-gel precipition method. The system AL2O3_Zr2O4
was obtained by mixing tow gel of alumina and zirconia precipited from aqueous solut
ions
of alumina nitrate and zirconium chlorid using ammonium hydroxide solution as precipited
agent. The system after mixing was allwed to settle for 24 h. The resuling precipitate was
filtered off and washed several times with deionized water and dried at 120°C for 24 h.
The powdered oven-dried hydrous alumina_zirconia was immersed in ammonium sulfate
solution(1) M for 24 h to incorporate sulfate ions. The resulting sample was dried at 120°
C for 24 h, calcined at 550°C for 6 h. The textural properties were determined by terating
of adsorption data of N2 at 77 K, and the results showed the changings in the textural
properties.The TG_DTA analysis showed the thermal stable of the samples in a long rang
of temperature. FTIR spectra showed that the sulfate ions were incorperated in the saples.
Some samples of alumina supporting with sulfate ions and molybdenium were
prepared by impregnation method. Supported samples were calcinated at 550°C for 6h.
Presence of sulfate ions and molybdenium lead to decreasing of the specific surface area o
f
alumina, and in the ease of molybdenium the decreasing value was higher. The total pore
volume was decreased with the pore size was increased. XRD patterns showed that the
incorporation of sulfate ions and molybdenium did not affect crystalin structure of
alumina. FTIR spectra showed the bonding between sulfate ionsmolybdenium
and
alumina. The TG-DTA studies showed that the losses mass was decreased when the sulfate
ions and molybdenium were incorporated, sulfate ions and molybdenium oxide
decomposed at ~700°C and ~800°C respectively .