Suppression of acoustic emission during superelastic tensile cycling of polycrystalline Ni$_{50.4}$Ti$_{49.6}$

85   0   0.0 ( 0 )
 نشر من قبل Guillaume Nataf
 تاريخ النشر 2020
  مجال البحث فيزياء
والبحث باللغة English




اسأل ChatGPT حول البحث

We investigate acoustic emission (AE) that arises during the martensitic transition in a polycrystalline specimen of the prototypical superelastic/elastocaloric alloy Ni$_{50.4}$Ti$_{49.6}$ (at. %) driven using tensile strain. We use two independent AE sensors in order to locate AE events, and focus on contributions to the AE that arise away from the grips of the mechanical testing machine. Significant AE activity is present during the first mechanical loading primarily due to nucleation and growth of wide Luders-like bands during the forward martensitic transition (imaged using visible light and infrared (IR) radiation) that lead to persistent changes in intergranular interactions. AE activity is suppressed during the subsequent reverse martensitic transition on unloading, and in successive loading/unloading cycles, for which the Luders-like bands narrow and modify intergranular interactions to much less extent. After the first loading, we find that the AE activity associated with the martensitic transition is weak, and we suggest that this is because the elastic anisotropy and strain incompatibility in Ni-Ti are low. We also find that the AE activity becomes weaker on mechanically cycling due to increased retained martensite.



قيم البحث

اقرأ أيضاً

Stress-induced martensitic transformations enable metastable alloys to exhibit enhanced strain hardening capacity, leading to improved formability and toughness. As is well-known from transformation-induced plasticity (TRIP) steels, however, the resu lting martensite can limit ductility and fatigue life due to its intrinsic brittleness. In this work, we explore an alloy design strategy that utilizes stress-induced martensitic transformations but does not retain the martensite phase. This strategy is based on the introduction of superelastic nano-precipitates, which exhibit reverse transformation after initial stress-induced forward transformation. To this end, utilizing ab-initio simulations and thermodynamic calculations we designed and produced a V45Ti30Ni25 (at%) alloy. In this alloy, TiNi is present as nano-precipitates uniformly distributed within a ductile V-rich base-centered cubic (bcc) beta matrix, as well as being present as a larger matrix phase. We characterized the microstructure of the produced alloy using various scanning electron microscopy (SEM) and transmission electron microscopy (TEM) methods. The bulk mechanical properties of the alloy are demonstrated through tensile tests, and the reversible transformation in each of the TiNi morphologies were confirmed by in-situ TEM micro-pillar compression experiments, in-situ high-energy diffraction synchrotron cyclic tensile tests, indentation experiments, and differential scanning calorimetry experiments. The observed transformation pathways and variables impacting phase stability are critically discussed
99 - Valerie Brien 2020
Pulsed laser deposition from a Nd:YAG laser was employed in production of hundreds of nanometer thick quasicrystalline Ti-Zr-Ni films on glass substrate. The influence of deposition temperature Ts on the structure, morphology and microstructure of th e films across their thickness was investigated. The morphology and microstructure features were evaluated by X-ray diffraction and transmission electron microscopy techniques. The low deposition temperatures were found to produce films with nanometer sized grains embedded in an amorphous matrix. The grains exhibit quasicrystalline order. The higher deposition temperatures lead to films whose structure is not uniform all along the growth direction. The layer in contact with the substrate is a very thin amorphous layer. The main part of the film consists of crystallized columns. The columns have grown from a nano-crystallized layer where the size of crystallites increases with increasing thickness.
We report magnetization and differential thermal analysis measurements as a function of pressure accross the martensitic transition in magnetically superelastic Ni-Mn-In alloys. It is found that the properties of the martensitic transformation are si gnificantly affected by the application of pressure. All transition temperatures shift to higher values with increasing pressure. The largest rate of temperature shift with pressure has been found for Ni$_{50}$Mn$_{34}$In$_{16}$ as a consequence of its small entropy change at the transition. Such a strong pressure dependence of the transition temperature opens up the possibility of inducing the martensitic transition by applying relatively low hydrostatic pressures.
Neutron scattering and ultrasonic methods have been used to study the lattice dynamics of two single crystals of Ni-Mn-In Heusler alloys close to Ni$_{50}$Mn$_{34}$In$_{16}$ magnetic superelastic composition. The paper reports the experimental determ ination of the low-lying phonon dispersion curves and the elastic constants for this alloy system. We found that the frequencies of the TA$_{2}$ branch are relatively low and it exhibits a small dip anomaly at a wave number $xi_{0} approx 1/3$, which softens with decreasing temperature. Associated with the softening of this phonon, we also observed the softening of the shear elastic constant $C=(C_{11}-C_{12})/2$. Both temperature softenings are typical for bcc based solids which undergo martensitic transformations and reflect the dynamical instability of the cubic lattice against shearing of ${110}$ planes along $<1bar{1}0>$ directions. Additionally, we measured low-lying phonon dispersion branches and elastic constants in applied magnetic fields aimed to characterize the magnetoelastic coupling.
Second harmonic generation amplitude and phase measurements are acquired in real time from fused silica:water interfaces that are subjected to ionic strength transitions conducted at pH 5.8. In conjunction with atomistic modeling, we identify correla tions between structure in the Stern layer, encoded in the total second-order nonlinear susceptibility, chi(2)tot, and in the diffuse layer, encoded in the product of chi(2)tot and the total interfacial potential, phi(0)tot. chi(2)tot:phi(0)tot correlation plots indicate that the dynamics in the Stern and diffuse layers are decoupled from one another under some conditions (large change in ionic strength), while they change in lockstep under others (smaller change in ionic strength) as the ionic strength in the aqueous bulk solution varies. The quantitative structural and electrostatic information obtained also informs on the molecular origin of hysteresis in ionic strength cycling over fused silica. Atomistic simulations suggest a prominent role of contact ion pairs (as opposed to solvent-separated ion pairs) in the Stern layer. Those simulations also indicate that net water alignment is limited to the first 2 nm from the interface, even at 0 M ionic strength, highlighting waters polarization as an important contributor to nonlinear optical signal generation.
التعليقات
جاري جلب التعليقات جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها
mircosoft-partner

هل ترغب بارسال اشعارات عن اخر التحديثات في شمرا-اكاديميا