We report frictional drag measurements between two superconducting LaAlO$_3$/SrTiO$_3$ nanowires. In these experiments, current passing through one nanowire induces a voltage across a nearby electrically isolated nanowire. The frictional drag signal contains both symmetric and antisymmetric components. The antisymmetric component arises from the rectification of quantum shot noise in the drive nanowire by the broken symmetry in the drag nanowire. The symmetric component in the drag resistance is ascribed to rectification of thermal noise in the drive nanowire during superconducting-normal transition. The suppression of the symmetric component is observed when a normal nanowire is used as either a drag or drive nanowire with the other nanowire superconducting. The absence of symmetric drag resistance between a normal drag nanowire and a superconducting drive nanowire suggests a higher electron-hole asymmetry in the superconducting LaAlO$_3$/SrTiO$_3$ nanowire arising from the 1D nature of superconductivity at LaAlO$_3$/SrTiO$_3$ interface.
A number of recent studies indicate that the charge conduction of the LaAlO$_3$/SrTiO$_3$ interface at low temperature is confined to filaments which are linked to structural domain walls in the SrTiO$_3$ with drastic consequences for example for the
The transport and thermoelectric properties of the interface between SrTiO$_3$ and a 26-monolayer thick LaAlO$_3$-layer grown at high oxygen-pressure have been investigated at temperatures from 4.2 K to 100 K and in magnetic fields up to 18 T. For $T
We describe the transport properties of mesoscopic devices based on the two dimensional electron gas (2DEG) present at the LaAlO$_3$/SrTiO$_3$ interface. Bridges with lateral dimensions down to 500~nm were realized using electron beam lithography. Th
At the LaAlO$_3$-SrTiO$_3$ interface, electronic phase transitions can be triggered by modulation of the charge carrier density, making this system an excellent prospect for the realization of versatile electronic devices. Here, we report repeatable
Novel physical phenomena arising at the interface of complex oxide heterostructures offer exciting opportunities for the development of future electronic devices. Using the prototypical LaAlO$_3$/SrTiO$_3$ interface as a model system, we employ a sin