تسجيل مستخدم جديدPressure-induced superconductivity in the giant Rashba system BiTeI
80
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
At ambient pressure, BiTeI is the first material found to exhibit a giant Rashba splitting of the bulk electronic bands. At low pressures, BiTeI undergoes a transition from trivial insulator to topological insulator. At still higher pressures, two structural transitions are known to occur. We have carried out a series of electrical resistivity and AC magnetic susceptibility measurements on BiTeI at pressure up to ~40 GPa in an effort to characterize the properties of the high-pressure phases. A previous calculation found that the high-pressure orthorhombic P4/nmm structure BiTeI is a metal. We find that this structure is superconducting with Tc values as high as 6 K. AC magnetic susceptibility measurements support the bulk nature of the superconductivity. Using electronic structure and phonon calculations, we compute Tc and find that our data is consistent with phonon-mediated superconductivity.
قيم البحث
اقرأ أيضاً
We observe a giant spin-orbit splitting in bulk and surface states of the non-centrosymmetric semiconductor BiTeI. We show that the Fermi level can be placed in the valence or in the conduction band by controlling the surface termination. In both cas
es it intersects spin-polarized bands, in the corresponding surface depletion and accumulation layers. The momentum splitting of these bands is not affected by adsorbate-induced changes in the surface potential. These findings demonstrate that two properties crucial for enabling semiconductor-based spin electronics -- a large, robust spin splitting and ambipolar conduction -- are present in this material.
High-pressure electrical resistance measurements have been performed on single crystal Ba0.5Sr0.5Fe2As2 platelets to pressures of 16 GPa and temperatures down to 10 K using designer diamond anvils under quasi-hydrostatic conditions with an insulating
steatite pressure medium. The resistance measurements show evidence of pressure-induced superconductivity with an onset transition temperature at ~31 K and zero resistance at ~22 K for a pressure of 3.3 GPa. The transition temperature decreases gradually with increasing in pressure before completely disappearing for pressures above 12 GPa. The present results provide experimental evidence that a solid solution of two 122-type materials, e.g., Ba1-x.SrxFe2As2 (0 < x <1), can also exhibit superconductivity under high pressure
The rich phenomena in the FeSe and related compounds have attracted great interests as it provides fertile material to gain further insight into the mechanism of high temperature superconductivity. A natural follow-up work was to look into the possib
ility of superconductivity in MnSe. It was shown that MnP becomes superconducting with Tc ~ 1 K under pressure. We demonstrated in this work that high pressure can effectively suppress the complex magnetic characters of MnSe crystal when observed at ambient condition. MnSe under pressure is found to undergo several structural transformations: the cubic phase first partially transforms to the hexagonal phase at about 12 GPa, the crystal exhibits the coexistence of cubic, hexagonal and orthorhombic phases from 16 GPa to 30 GPa, and above 30 GPa the crystal shows a single orthorhombic phase. Superconductivity with Tc ~ 5 K was first observed at pressure ~12 GPa by magnetic measurements (~16 GPa by resistive measurements). The highest Tc is ~ 9 K (magnetic result) at ~35 GPa. Our observations suggest the observed superconductivity may closely relate to the pressure-induced structural change. However, the interface between the metallic and insulating boundaries may also play an important role to the pressure induced superconductivity in MnSe.
Layered ternary transition-metal chalcogenides have been focused as a vein of exploration for superconductors. In this study, TiGeTe$_{6}$ single crystals were synthesized and characterized by structural and valence state analyses and electrical tran
sport measurements. The transport properties were measured under various pressures up to 71 GPa. The activation energy gets smaller as the applied pressure increases, and a signature of a pressure-induced metallization was observed under around 8.4 GPa. Under 13 GPa, pressure-induced superconductivity was discovered in this compound for the first time, with successive drops at 3 K and 6 K in the resistance, indicating the presence of multiple superconducting transitions. The superconducting transition temperature kept increasing as we further applied the pressure to the TiGeTe$_{6}$ single crystal in the performed pressure range, reaching as high as 8.1 K under 71 GPa.
Bi2Te3 compound has been theoretically predicted (1) to be a topological insulator, and its topologically non-trivial surface state with a single Dirac cone has been observed in photoemission experiments (2). Here we report that superconductivity (Tc
^~3K) can be induced in Bi2Te3 as-grown single crystal (with hole-carriers) via pressure. The first-principles calculations show that the electronic structure under pressure remains to be topologically nontrivial, and the Dirac-type surface states can be well distinguished from bulk states at corresponding Fermi level. The proximity effect between superconducting bulk states and Dirac-type surface state could generate Majorana fermions on the surface. We also discuss the possibility that the bulk state could be a topological superconductor.