تسجيل مستخدم جديدMOD derived pyrochlore films as buffer layer for all-chemical YBCO coated conductors
143
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
We report a detailed study performed on La2Zr2O7 (LZO) pyrochlore material grown by Metal-Organic Decomposition (MOD) method as buffer layers for YBa2Cu3O7-x (YBCO) coated conductors. High quality epitaxial LZO thin films have been obtained on single crystal (SC) and Ni-5%at.W substrates. In order to evaluate structural and morphological properties, films have been characterized by means of X-ray diffraction analyses (XRD), atomic force microscope (AFM) and scanning electron microscope (SEM). Precursors solutions and heat treatments have been studied by thermogravimetric analyses (TG-DTA-DTG) and infrared spectra (FT-IR) with the aim of optimizing the annealing process. Thin films of YBCO have been deposited by pulsed laser ablation (PLD) on this buffer layers. The best results obtained on SC showed YBCO films with critical temperature values above 90 K, high self field critical current density values (Jc > 1 MA/cm2) and high irreversibility field values (8.3 T) at 77 K together with a rather high depinning frequency vp (0.5 T, 77 K)>44 GHz as determined at microwaves. The best results on Ni-5%at.W has been obtained introducing in the heat treatment a pyrolysis process at low temperature in air in order to remove the residual organic part of the precursor solution.
قيم البحث
اقرأ أيضاً
We present a comparative study of the angular dependent critical current density in YBa2Cu3O7 films deposited on IBAD MgO and on single crystal MgO and SrTiO3 substrates. We identify three angular regimes where pinning is dominated by different types
of correlated and uncorrelated defects. We show that those regimes are present in all cases, indicating that the pinning mechanisms are the same, but their extension and characteristics are sample dependent, reflecting the quantitative differences in texture and defect density. In particular, the more defective nature of the films on IBAD turns into an advantage as it results in stronger vortex pinning, demonstrating that the critical current density of the films on single crystals is not an upper limit for the performance of the IBAD coated conductors.
High temperature superconducting coated conductor (CC) could be practically applied in electric equipment due to its favorable mechanical properties and the critical current performance of YBCO superconducting layer. It is well known that CC could be
easily delaminated because of its poor stress tolerance in thickness direction, i.e. along the c-axis of YBCO. Commonly, a stack including YBCO layer and silver stabilizer could be obtained after the delamination. It would be interesting to investigate the superconducting properties of the delaminated stack, since it could also be considered as a new type of CC with the silver stabilizer as the buffer layer, which is quite different from the oxide buffer layers in the traditional CC and might lead to new applications. In this study, a CC sample was delaminated by liquid nitrogen immersing. A Hall probe scanning system was employed to measure the critical current (IC) distribution of the original sample and the obtained stack. It was found that IC could be partially preserved after the delamination. Dense and crack-free morphologies of the delaminated surfaces were observed by scanning electron microscopy, and the potential application of the obtained stack in superconducting joint technology was discussed.
Structural and superconducting properties of magnesium diboride thin films grown by pulsed laser deposition on zirconium diboride buffer layers were studied. We demonstrate that the ZrB2 layer is compatible with the MgB2 two step deposition process.
Synchrotron radiation measurements, in particular anomalous diffraction measurements, allowed to separate MgB2 peaks from ZrB2 ones and revealed that both layers have a single in plane orientation with a sharp interface between them. Moreover, the buffer layer avoids oxygen contamination from the sapphire substrate. The critical temperature of this film is near 37.6 K and the upper critical field measured at Grenoble High Magnetic Field Laboratory up to 20.3 T is comparable with the highest ones reported in literature.
It is shown that the critical currents of high-Tc superconducting tapes fabricated by the coated conductor technologies are enhanced considerably if grain arrangements with large effective grain boundary areas are used. Increasing the aspect ratios o
f the grains reduces the deleterious effects of the grain boundaries. A practical road to competitive high-Tc cables is proposed.
The critical currents of MOD/RABiTS and PLD/IBAD coated conductors have been measured as a function of magnetic field orientation and compared to films grown on single crystal substrates. By varying the orientation of magnetic field applied in the pl
ane of the film, we are able to determine the extent to which current flow in each type of conductor is percolative. Standard MOD/RABiTS conductors have also been compared to samples whose grain boundaries have been doped by diffusing Ca from an overlayer. We find that undoped MOD/RABiTS tapes have a less anisotropic in-plane field dependence than PLD/IBAD tapes and that the uniformity of critical current as a function of in-plane field angle is greater for MOD/RABiTS samples doped with Ca.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها