MgB2 is a promising superconductor for important large-scale applications for both high field magnets and cryocooler-cooled magnet operated at temperatures around 20 K. In this work, by utilizing C60 as a viable alternative dopant, we demonstrate a simple and industrially scaleable rout that yields a 10-15-fold improvement in the in-high-field current densities of MgB2 tape conductors. For example, a Jc value higher than 4x10^4 A/cm^2 (4.2 K, 10 T), which exceeds that for NbTi superconductor, can be realized on the C60 doped MgB2 tapes. It is worth noting that this value is even higher than that fabricated using strict high energy ball milling technique under Ar atmosphere. At 20 K, Hirr was about 10 T for C60 doped MgB2 tapes. A large amount of nanometer-sized precipitates and grain boundaries were found in MgB2 matrix. The special physical and chemical characteristic of C60, in addition to its C containing intrinsic essence, is a key point in enhancing the superconducting performance of MgB2 tapes.
قيم البحث
اقرأ أيضاً
We investigated the effect of nanoscale-C doping on the critical current density Jc and irreversibility field Birr of Fe-sheathed MgB2 tapes prepared by the in-situ powder-in-tube method. The tapes were heat treated at 600-950C for 1 h. Higher values
of Jc and Birr were seen for 5 at.%C-doped MgB2 tapes at higher sintering temperatures, where substantial substitution of boron for carbon occurred. The C-doped samples sintered at 950C showed the highest Birr, for example, at 4.2 K, the Birr reached 22.9 T. In particular, at 20 K, Birr for the C-doped tape achieved 9 T, which is comparable to the upper critical field of the commercial NbTi at 4.2 K. This role of nano-sized C particles can be very beneficial in the fabrication of MgB2 tapes for magnetic resonance imaging applications at 20 K.
There are numerous potential applications for superconducting tapes, based on YBa2Cu3O7-x (YBCO) films coated onto metallic substrates. A long established goal of more than 15 years has been to understand the magnetic flux pinning mechanisms which al
low films to maintain high current densities out to high magnetic fields. In fact, films carry 1-2 orders of magnitude higher current densities than any other form of the material. For this reason, the idea of further improving pinning has received little attention. Now that commercialisation of conductors is much closer, for both better performance and lower fabrication costs, an important goal is to achieve enhanced pinning in a practical way. In this work, we demonstrate a simple and industrially scaleable route which yields a 1.5 to 5-fold improvement in the in-field current densities of already-high-quality conductors.
Fe-clad MgB2 long tapes have been fabricated using a powder-in-tube technique. An Mg + 2B mixture was used as the central conductor core and reacted in-situ to form MgB2. The tapes were sintered in pure Ar at 800 ^(o) C for 1 h at ambient pressure. S
EM shows a highly dense core with a large grain size of 100 micron. The Fe clad tape shows a sharp transition with transition width of 0.2 K and Tc0 at 37.5 K. We have achieved the highest transport critical current reported so far at 1.6 times 10^(4) A/cm^2 for both 29.5 K in 1 Tesla and 33 K in null field. R-T and critical current were also measured for fields perpendicular and parallel to the tape plane. The iron cladding shielded on the core from the applied external field, with the shielding being less effective for the field in the tape plane. Fe cladding may be advantageous for some applications as it could reduce the effects of both the self-field and external fields.
MgB2/Fe tapes with 2.5-15 at.% ZrB2 additions were prepared through the in situ powder-in-tube method. Compared to the pure tape, a significant improvement in the in-field critical current density Jc was observed, most notably for 10 at.% doping, whi
le the critical temperature decreased slightly. At 4.2 K, the transport Jc for the 10 at.% doped sample increased by more than an order of magnitude than the undoped one in magnetic fields above 9 T. Nanoscale segregates or defects caused by the ZrB2 additions which act as effective flux pinning centers are proposed to be the main reason for the improved Jc field performance.
The paper reports the first successful fabrication of MgB2 superconducting tape using a flexible metallic substrate as well as its strong pinning force, which was verified by direct measurement of transport critical current density. The tape was prep
ared by depositing MgB2 film on a Hastelloy tape buffered with an YSZ layer. The Jc of the tape exceeds 105A/cm2 at 4.2K and 10T, which is considered as a common benchmark for magnet application. The Jc dependence on magnetic field remains surprisingly very small up to 10T, suggesting that the tape has much better magnetic field characteristic than conventional Nb-Ti wires in liquid helium.