The effect of surface degradation of the thermolectric cobaltite on Raman spectra is discussed and compared to experimental results from Co3O4 single crystals. We conclude that on NaCl flux grown NaxCoO2 crystals a surface layer of Co3O4 easily forms that leads to the observation of an intense phonon around 700 cm-1 [Phys. Rev. B 70, 052502 (2004)]. Raman spectra on freshly cleaved crystals from optical floating zone ovens do not show such effects and have a high frequency phonon cut-off at approximately 600 cm -1 [Phys. Rev. Lett 96, 167204 (2006)]. We discuss the relation of structural dimensionality, electronic correlations and the high frequency phonon cut-off of the thermolectric cobaltite.
قيم البحث
اقرأ أيضاً
The Raman spectra of the parent compound NaxCoO2 (x=0.75) and the superconducting oxyhydrates NaxCoO2.yH2O with different superconducting temperatures (Tc) have been measured. Five Raman active phonons around 195 cm-1 (E1g), 482 cm-1, 522 cm-1, 616 c
m-1 (3E2g), 663 cm-1 (A1g) appear in all spectra. These spectra change systematically along with the intercalation of H2O and superconducting properties. In particular, the Raman active phonons (A1g and E1g) involving the oxygen motions within the Co-O layers show up monotonous decrease in frequency along with superconducting temperature Tc. The fundamental properties and alternations of other active Raman phonons in the superconducting materials have also been discussed.
The electronic properties of Co in bulk Na0.7CoO2 and the superconducting hydrated compound Na0.35CoO2 - y H2O have been investigated by x-ray absorption spectroscopy (XAS) and resonant inelastic x-ray scattering (RIXS) using hard x-rays. The XAS spe
ctra at the Co K-edge were measured in both compounds with two different polarization directions. The changes in the XAS spectra upon hydration and their polarization dependence are well accounted for by linear muffin- tin orbital calculations in the local density approximation. The underlying electronic structure indicates the strong hybridization between the Co 3d and O 2p states in both compounds, while the electron localization is enhanced in the hydrated compound due to the increase of the Co-Co interplanar distance. The Co K pre-edge further highlights the splitting of the d band as a result of the crystal field effect and demonstrates the Co valency increase when Na0.7CoO2 is hydrated. The RIXS spectra measured at the Co K-edge show an energy loss feature around 10 eV in both compounds in fair agreement with the calculated dynamical structure factor. The RIXS feature is associated to a damped plasmon excitation.
We synthesized Nax(H3O)zCoO2yH2O samples with various Na/H3O ratios but with the constant Co valence of s = +3.40, and measured their magnetic properties to draw phase diagrams of the system. The superconductivity is very sensitive to the Na/H3O rati
o. With varying x under fixed s of +3.40, magnetically ordered phase appears in the intermediate range of x sandwiched by two separated superconducting phases, suggesting that the superconductivity is induced by moderately strong magnetic interactions. In the vicinity of the magnetic phase, transition from the superconducting state to the magnetically ordered state was induced by applying high magnetic field. This transition is of the second order, at least, above 1.8 K. The upper-critical field is expected to be much higher than the Pauli limit for a phase located far away from the magnetic phase regarding the Na/H3O ratio.
We synthesized powder samples of Na$_{x}$CoO$_{2}cdot y$H$_{2}$O changing the volume of the water in the hydration process, then investigated their superconducting properties,. It was proved that the volume of water is one of key parameters to obtain
a single phase of Na$_{x}$CoO$_{2}cdot y$H$_{2}$O with good superconducting properties. The transition temperature, $T_{c}$, of the sample changed gradually while it was stored in the atmosphere of 70% humidity. Superconducting behavior under high magnetic field was very sensitive to $T_{c}$. $H_{c2}$ of a high quality sample with high $T_{c}$ seemed very high.
The results of DC magnetization measurements under hydrostatic (helium-gas) pressure are reported for an ambient pressure superconductor Na0.35CoO2.1.4D2O and its precursor compound, the gamma-phase Na0.75CoO2 that is known to combine a metallic cond
uctivity with an unusual magnetic state below ~22K. The obtained data allowed us to present for the first time the pressure dependence of the magnetic transition in a metallic sodium cobaltate system. This dependence appears to be positive, with the magnetic transition rapidly shifting towards higher temperatures when an applied pressure increases. We ascribe the observed effect to the pressure-induced enhancement of the out-of-plane antiferromagnetic coupling mediated by localized spins interactions (of either superexchange or RKKY type), the scenario consistent with the A-type antiferromagnetic state suggested by recent neutron-scattering data. As for the pressure effect on the superconductivity in Na0.35CoO2.1.4D2O, our measurements established negative and linear for the entire pressure range from 1 bar to 8.3 kbar pressure dependence of Tc, the behavior quite different from the reported by previous workers strong non-linearity of the Tc (P) dependence. (Dated September 12, 2005) PACS numbers: 74.62.Fj, 74.70.-b, 75.20. En, 75.50 Ee, 75.30 Kz.