تسجيل مستخدم جديدEquipartition of Current in Parallel Conductors on Cooling Through the Superconducting Transition
109
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
Our experiments show that for two or more pieces of a wire, of different lengths in general, combined in parallel and connected to a dc source, the current ratio evolves towards unity as the combination is cooled to the superconducting transition temperature Tc, and remains pinned at that value below it. This re-distribution of the total current towards equipartition without external fine tuning is a surprise. It can be physically understood in terms of a mechanism that involves the flux-flow resistance associated with the transport current in a wire of type-II superconducting material. It is the fact that the flux-flow resistance increases with current that drives the current division towards equipartition.
قيم البحث
اقرأ أيضاً
The critical currents of MOD/RABiTS and PLD/IBAD coated conductors have been measured as a function of magnetic field orientation and compared to films grown on single crystal substrates. By varying the orientation of magnetic field applied in the pl
ane of the film, we are able to determine the extent to which current flow in each type of conductor is percolative. Standard MOD/RABiTS conductors have also been compared to samples whose grain boundaries have been doped by diffusing Ca from an overlayer. We find that undoped MOD/RABiTS tapes have a less anisotropic in-plane field dependence than PLD/IBAD tapes and that the uniformity of critical current as a function of in-plane field angle is greater for MOD/RABiTS samples doped with Ca.
The in-field critical current of commercial YBa2Cu3O7 coated conductors can be substantially enhanced by post-fabrication irradiation with 4 MeV protons. Irradiation to a fluence of 8x10^16 p/cm^2 induces a near doubling of the critical current in fi
elds of 6 T || c at a temperature of 27 K, a field and temperature range of interest for applications such as rotating machinery. A mixed pinning landscape of preexisting precipitates and twin boundaries and small, finely dispersed irradiation induced defects may account for the improved vortex pinning in high magnetic fields. Our data indicate that there is significant head-room for further enhancements.
We present a combined experimental and theoretical study of the effects of pressure on T_c of the hexagonal layered superconductors nH-CaAlSi (n = 1, 5, 6), where nH labels the different stacking variants that were recently discovered. Experimentally
, the pressure dependence of T_c has been investigated by measuring the magnetic susceptibility of single crystals up to 10 kbar. In contrast to previous results on polycrystalline samples, single crystals with different stacking sequences display different pressure dependences of T_c. 1H-CaAlSi shows a decrease of T_c with pressure, whereas 5H and 6H-CaAlSi exhibit an increase of T_c with pressure. Ab-initio calculations for 1H, 5H and 6H -CaAlSi reveal that an ultrasoft phonon branch associated to out-of-plane vibrations of the Al-Si layers softens with pressure, leading to a structural instability at high pressures. For 1H-CaAlSi the softening is not sufficient to cause an increase of T_c, which is consistent with the present experiments, but adverse to previous reports. For 5H and 6H the softening provides the mechanism to understand the observed increase of T_c with pressure. Calculations for hypothetical 2H and 3H stacking variants reveal qualitative and quantitative differences.
A rapid decrease in the critical current density (Jc) of YBa2Cu3O7-x (YBCO) films with increasing film thickness has been observed for multiple YBCO growth processes. While such behavior is predicted from 2D collective pinning models under certain as
sumptions, empirical observations of the thickness dependence of Jc are believed to be largely processing dependent at present. To investigate this behavior in ex situ YBCO films, 2.0 and 2.9 um thick YBCO films on ion beam assisted deposition (IBAD) - yttria stabilized zirconia (YSZ) substrates were thinned and repeatedly measured for rho(T) and Jc(H). The 2.9 um film exhibited a constant Jc(77K,SF) through thickness of ~1 MA/cm2 while the 2.0 um film exhibited an increase in Jc(77K,SF) as it was thinned. Neither film offered evidence of significant dead layers, suggesting that further increases in critical current can be obtained by growing thicker YBCO layers.
There are numerous potential applications for superconducting tapes, based on YBa2Cu3O7-x (YBCO) films coated onto metallic substrates. A long established goal of more than 15 years has been to understand the magnetic flux pinning mechanisms which al
low films to maintain high current densities out to high magnetic fields. In fact, films carry 1-2 orders of magnitude higher current densities than any other form of the material. For this reason, the idea of further improving pinning has received little attention. Now that commercialisation of conductors is much closer, for both better performance and lower fabrication costs, an important goal is to achieve enhanced pinning in a practical way. In this work, we demonstrate a simple and industrially scaleable route which yields a 1.5 to 5-fold improvement in the in-field current densities of already-high-quality conductors.