Bulk and surface properties of high-quality single crystals of zirconium dodecaboride have been studied in the temperature range from 4.5 K up to the superconducting transition temperature which is found to be nearly 6.06 K. Scanning tunnelling spectroscopy data, together with dc and ac magnetization measurements, are consistent with the conventional s-wave pairing scenario, whereas they disagree in estimates of the electron-phonon coupling strength. We explain the divergence, supposing a great difference between the surface and bulk superconducting characteristics of the compound. This assertion is supported by our findings of a non-linear magnetic response to an amplitude-modulated alternating magnetic field, testifying to the presence of surface superconductivity in the ZrB$_{12}$ samples at dc fields exceeding the thermodynamic critical field.
We report experimental studies of the low frequency electrodynamics of ZrB$_{12}$ and Nb single crystals. AC susceptibility at frequencies 3 - 1000 Hz have been measured under a dc magnetic field, $H_0$, applied parallel to the sample surface. In the
The large nonlinear response of a single crystal ZrB$_{12}$ to an ac field (frequency 40 - 2500 Hz) for $H_0>H_{c2}$ has been observed. Direct measurements of the ac wave form and the exact numerical solution of the Ginzburg-Landau equations, as well
The results of the comprehensive ultrasonic research of high quality single crystals of FeSe are presented. Absolute values of sound velocities and their temperature dependences were measured; elastic constants and Debye temperature were calculated.
We report optical (6 meV - 4 eV) properties of a boride superconductor ZrB$_{12}$ ($T_c$ = 6 K) in the normal state from 20 to 300 K measured on high-quality single crystals by a combination of reflectivity and ellipsometry. The Drude plasma frequenc
Single crystals of RbOs2O6 have been grown from Rb2O and Os in sealed quartz ampoules. The crystal structure has been identified at room temperature as cubic with the lattice constant a = 10.1242(12) A. The anisotropy of the tetrahedral and octahedra