تسجيل مستخدم جديدMagnetic-field-induced collapse of charge-ordered nanoclusters and the Colossal Magnetoresistance effect in Nd(0.3)Sr(0.3)MnO(3)
148
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
We report synchrotron x-ray scattering studies of charge/orbitally ordered (COO) nanoclusters in Nd$_{0.7}$Sr$_{0.3}$MnO$_3$. We find that the COO nanoclusters are strongly suppressed in an applied magnetic field, and that their decreasing concentration follows the field-induced decrease of the sample electrical resistivity. The COO nanoclusters, however, do not completely disappear in the conducting state, suggesting that this state is inhomogeneous and contains an admixture of an insulating phase. Similar results were also obtained for the zero-field insulator-metal transition that occurs as temperature is reduced. These observations suggest that these correlated lattice distortions play a key role in the Colossal Magnetoresistance effect in this prototypical manganite.
قيم البحث
اقرأ أيضاً
A field-induced crossover is observed in the resistivity and magnetization (M) of a La(0.7)Pb(0.3)MnO(3) single crystal. The field-dependence of the resistivity and M suggests that a small spin-canted species with mean-field-like interactions dominat
es at low fields (H), whereas, individual spins and 3D Ising/Heisenberg models describe the high-H behavior rather well. Around the ferromagnetic transition, an H-induced destruction of the small spin-canted magnetic polarons is accompanied by large magnetoresistance.
We report on first principles calculations of the electronic structure of La$_{0.7}$Sr$_{0.3}$MnO$_{3}$/SrTiO$_{3}$ junction with two possible types of interface terminations. We find that the La$_{0.7}$Sr$_{0.3}$O/TiO$_{2}$ interface preserves the i
nterlayer ferromagnetic coupling between the interface MnO$_{2}$ layer and the bulk. The other interface, MnO$_{2}$/SrO, favours antiferromagnetic coupling with the bulk. By inserting two unit cells of undoped LaMnO$_{3}$ at the interface the ferromagnetism is recovered. This is understood in terms of the doping level and the mobility of carriers near the interface.
Charge transfer induced interfacial ferromagnetism and its impact on the exchange bias effect in La$_{0.7}$Sr$_{0.3}$MnO$_3$/NdNiO$_3$ correlated oxide heterostructures were investigated by soft x-ray absorption and x-ray magnetic circular dichroism
spectra in a temperature range from 10 to 300 K. Besides the antiferromagnetic Ni$_3^+$ cations which are naturally part of the NdNiO$_3$ layer, Ni$_2^+$ ions are formed at the interface due to a charge transfer mechanism involving the Mn element of the adjacent layer. They exhibit a ferromagnetic behavior due to the exchange coupling to the Mn$_4^+$ ions in the La$_{0.7}$Sr$_{0.3}$MnO$_3$ layer. This can be seen as detrimental to the strength of the unidirectional anisotropy since a significant part of the interface does not contribute to the pinning of the ferromagnetic layer. By analyzing the line shape changes of the x-ray absorption at the Ni L$_{2,3}$ edges, the metal-insulator transition of the NdNiO$_3$ layer is resolved in an element specific manner. This phase transition is initiated at about 120 K, way above the paramagnetic to antiferromagnetic transition of NdNiO$_3$ layer which measured to be 50 K. Exchange bias and enhanced coercive fields were observed after field cooling the sample through the Neel temperature of the NdNiO$_3$ layer. Different from La$_{0.7}$Sr$_{0.3}$MnO$_3$/LaNiO$_3$, the exchange bias observed in La$_{0.7}$Sr$_{0.3}$MnO$_3$/NdNiO$_3$ is due to the antiferromagnetism of NdNiO$_3$ and the frustration at the interface. These results suggest that reducing the interfacial orbital hybridization may be used as a tunable parameter for the strength of the exchange bias effect in all-oxide heterostructures which exhibit a charge transfer mechanism.
Materials that exhibit colossal magnetoresistance (CMR) are currently the focus of an intense research effort, driven by the technological applications that their sensitivity lends them to. Using the angular correlation of photons from electron-posit
ron annihilation, we present a first glimpse of the Fermi surface of a material that exhibits CMR, supported by ``virtual crystal electronic structure calculations. The Fermi surface is shown to be sufficiently cubic in nature that it is likely to support nesting.
The magnetic dead layers in films a few nanometers thick are investigated for La$_{0.7}$Sr$_{0.3}$MnO$_3$ on (001)-oriented SrTiO$_3$ (STO), LaAlO$_3$ (LAO) and (LaAlO$_3$)$_{0.3}$(Sr$_2$TaAlO$_6$)$_{0.7}$ (LSAT) substrates. An anomalous moment found
to persist above the Curie temperature of the La$_{0.7}$Sr$_{0.3}$MnO$_3$ films is not attributed to the films, but to oxygen vacancies at or near the surface of the substrate. The contribution to the moment from the substrate is as high as 20 $mu$B/nm$^2$ in the case of STO or LSAT. The effect is increased by adding an STO cap layer. Taking this d-zero magnetism into account, extrapolated magnetic dead layer thicknesses of 0.8 nm, 1.5 nm and 3.0 nm are found for the manganite films grown on LSAT, STO and LAO substrates, respectively. An STO cap layer eliminates the LSMO dead layer.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها