Transition metal dichalcogenides (TMDs) have been a core constituent of 2D material research throughout the last decade. Over this time, research focus has progressively shifted from synthesis and fundamental investigations, to exploring their properties for applied research such as electrochemical applications and integration in electrical devices. Due to the rapid pace of development, priority is often given to application-oriented aspects while careful characterisation and analysis of the TMD materials themselves is occasionally neglected. This can be particularly evident for characterisations involving X-ray photoelectron spectroscopy (XPS), where measurement, peak-fitting, and analysis can be complex and nuanced endeavours requiring specific expertise. To improve the availability and accessibility of reference information, here we present a detailed peak-fitted XPS analysis of ten transition metal chalcogenides. The materials were synthesised as large-area thin-films on SiO2 using direct chalcogenisation of pre-deposited metal films. Alongside XPS, the Raman spectra with several excitation wavelengths for each material are also provided. These complementary characterisation methods can provide a more complete understanding of the composition and quality of the material. As material stability is a crucial factor when considering applications, the in-air thermal stability of the TMDs was investigated after several annealing points up to 400 {deg}C. This delivers a trend of evolving XPS and Raman spectra for each material which improves interpretation of their spectra while also indicating their ambient thermal limits. This provides an accessible library and set of guidelines to characterise, compare, and discuss TMD XPS and Raman spectra.
قيم البحث
اقرأ أيضاً
Cobalt nitride (Co-N) thin films prepared using a reactive magnetron sputtering process by varying the relative nitrogen gas flow (pn) are studied in this work. As pn~increases, Co(N), tcn, Co$_3$N and CoN phases are formed. An incremental increase i
n pn, after emergence of tcn~phase at pn=10p, results in a continuous expansion in the lattice constant ($a$) of tcn. For pn=30p, $a$ maximizes and becomes comparable to its theoretical value. An expansion in $a$ of tcn, results in an enhancement of magnetic moment, to the extent that it becomes even larger than pure Co. Though such higher (than pure metal) magnetic moment for Fe$_4$N thin films have been theoretically predicted and evidenced experimentally, higher (than pure Co) magnetic moment are evidenced in this work and explained in terms of large-volume high-moment model for tetra metal nitrides.
Atomically thin two-dimensional molybdenum disulfide (MoS2) sheets have attracted much attention due to their potential for future electronic applications. They not only present the best planar electrostatic control in a device, but also lend themsel
ves readily for dielectric engineering. In this work, we experimentally investigated the dielectric effect on the Raman and photoluminescence (PL) spectra of monolayer MoS2 by comparing samples with and without HfO2 on top by atomic layer deposition (ALD). Based on considerations of the thermal, doping, strain and dielectric screening influences, it is found that the red shift in the Raman spectrum largely stems from modulation doping of MoS2 by the ALD HfO2, and the red shift in the PL spectrum is most likely due to strain imparted on MoS2 by HfO2. Our work also suggests that due to the intricate dependence of band structure of monolayer MoS2 on strain, one must be cautious to interpret its Raman and PL spectroscopy.
In the present work, we systematically studied the effect of Al doping on the phase formation of iron nitride (Fe-N) thin films. Fe-N thin films with different concentration of Al (Al=0, 2, 3, 6, and 12 at.%) were deposited using dc magnetron sputter
ing by varying the nitrogen partial pressure between 0 to 100%. The structural and magnetic properties of the films were studied using X-ray diffraction and polarized neutron reflectivity. It was observed that at the lowest doping level (2 at.% of Al), nitrogen rich non-magnetic Fe-N phase gets formed at a lower nitrogen partial pressure as compared to the un-doped sample. Interestingly, we observed that as Al doping is increased beyond 3at.%, nitrogen rich non-magnetic Fe-N phase appears at higher nitrogen partial pressure as compared to un-doped sample. The thermal stability of films were also investigated. Un-doped Fe-N films deposited at 10% nitrogen partial pressure possess poor thermal stability. Doping of Al at 2at.% improves it marginally, whereas, for 3, 6 and 12at.% Al doping, it shows significant improvement. The obtained results have been explained in terms of thermodynamics of Fe-N and Al-N.
This paper reports the synthesis and detailed characterization of graphite thin films produced by thermal decomposition of the (0001) face of a 6H-SiC wafer, demonstrating the successful growth of single crystalline films down to approximately one gr
aphene layer. The growth and characterization were carried out in ultrahigh vacuum (UHV) conditions. The growth process and sample quality were monitored by low-energy electron diffraction, and the thickness of the sample was determined by core level x-ray photoelectron spectroscopy. High-resolution angle-resolved photoemission spectroscopy shows constant energy map patterns, which are very sharp and fully momentum-resolved, but nonetheless not resolution limited. We discuss the implications of this observation in connection with scanning electron microscopy data, as well as with previous studies.
The synthesis of transition metal dichalcogenides (TMDs) has been a primary focus for 2D nanomaterial research over the last 10 years, however, only a small fraction of this research has been concentrated on transition metal ditellurides. In particul
ar, nanoscale platinum ditelluride (PtTe2) has rarely been investigated, despite its potential applications in catalysis, photonics and spintronics. Of the reports published, the majority examine mechanically-exfoliated flakes from chemical vapor transport (CVT) grown crystals. While this production method is ideal for fundamental studies, it is very resource intensive therefore rendering this process unsuitable for large scale applications. In this report, the synthesis of thin films of PtTe2 through the reaction of solid-phase precursor films is described. This offers a production method for large-area, thickness-controlled PtTe2, suitable for a range of applications. These polycrystalline PtTe2 films were grown at temperatures as low as 450 degC, significantly below the typical temperatures used in the CVT synthesis methods. To investigate their potential applicability, these films were examined as electrocatalysts for the hydrogen evolution reaction (HER) and oxygen reduction reaction (ORR). The films showed promising catalytic behavior, however, the PtTe2 was found to undergo chemical transformation to a substoichiometric chalcogenide compound under ORR conditions. This study shows while PtTe2 is stable and highly useful for HER, this property does not apply to ORR, which undergoes a fundamentally different mechanism. This study broadens our knowledge of the electrocatalysis of TMDs.