تسجيل مستخدم جديدUltrafast demagnetization in NiCo2O4 thin films probed by time-resolved microscopy
109
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
Using a time-resolved magneto-optical Kerr effect (TR-MOKE) microscope, we observed ultrafast demagnetization of inverse-spinel-type NiCo2O4 (NCO) epitaxial thin films of the inverse spinel type ferrimagnet NCO with perpendicular magnetic anisotropy. This microscope uses a pump-probe method, where the sample is pumped at 1030 nm, and magnetic domain images are acquired via MOKE microscopy at 515 nm (the second harmonic). We successfully observed the dynamics of the magnetic domain of the NCO thin film via laser irradiation, and obtained a demagnetization time constant of approximately 0.4 ps. This time constant was significantly smaller than the large time constants reported for other half-metallic oxides. These results, combined with the results of our x-ray photoemission spectroscopy study, indicate that this NCO thin film is a ferrimagnetic metal whose electronic structure deviates from the theoretically predicted half-metallic one.
قيم البحث
اقرأ أيضاً
We have investigated the ultrafast spin dynamics in EuO thin films by time-resolved Faraday rotation spectroscopy. The photoinduced magnetization is found to be increased in a transient manner, accompanied with subsequent demagnetization. The dynamic
al magnetization enhancement showed a maximum slightly below the Curie temperature with prolonged tails toward both lower and higher temperatures and dominates the demagnetization counterpart at 55 K. The magnetization enhancement component decays in ~1 ns. The realization of the transient collective ordering is attributable to the enhancement of the f-d exchange interaction.
Measuring terahertz (THz) conductivity on an ultrafast time scale is an excellent way to observe charge-carrier dynamics in semiconductors as a function of time after photoexcitation. However, a conductivity measurement alone cannot separate the effe
cts of charge-carrier recombination from effective mass changes as charges cool and experience different regions of the electronic band structure. Here we present a form of time-resolved magneto-THz spectroscopy which allows us to measure cyclotron effective mass on a picosecond time scale. We demonstrate this technique by observing electron cooling in the technologically-significant narrow-bandgap semiconductor indium antimonide (InSb). A significant reduction of electron effective mass from 0.032$m_mathrm{e}$ to 0.017$m_mathrm{e}$ is observed in the first 200ps after injecting hot electrons. Measurement of electron effective mass in InSb as a function of photo-injected electron density agrees well with conduction band non-parabolicity predictions from ab initio calculations of the quasiparticle band structure.
We examined the photo-induced dynamics of ferromagnetic Co/Pt thin films demonstrating perpendicular magnetic anisotropy with element specificity using resonant polar magneto-optical Kerr effect measurements at Pt~N${}_{6,7}$ and Co~M${}_{2,3}$ edges
with an x-ray free electron laser. The obtained results showed a clear element dependence of photo-induced demagnetization time scales: $tau_textrm{demag.}^textrm{Co}=80pm60~textrm{fs}$ and $tau_textrm{demag.}^textrm{Pt}=640pm140~textrm{fs}$. This dependence is explained by the induced moment of the Pt atom by current flow from the Co layer through the interfaces. The observed magnetization dynamics of Co and Pt can be attributed to the characteristics of photo-induced Co/Pt thin film phenomena including all-optical switching.
Despite the low resistivity (~ 1 mohm cm), the metallic electrical transport has not been commonly observed in the inverse spinel NiCo2O4, except in certain epitaxial thin films. Previous studies have stressed the effect of valence mixing and degree
of spinel inversion on the electric conduction of NiCo2O4 films. In this work, we have studied the effect of microstructure by comparing the NiCo2O4 epitaxial films grown on MgAl2O4 (111) and on Al2O3 (0001) substrates. Although the optimal growth condition and the magnetic properties are similar for the NiCo2O4/MgAl2O4 and the NiCo2O4/Al2O3, they show metallic and semiconducting electrical transport respectively. Despite similar temperature and field dependence of magnetization, the NiCo2O4/Al2O3 show much larger magnetoresistance at low temperature. Post-growth annealing decreases the resistivity of NiCo2O4/Al2O3, but the annealed films are still semiconducting. The correlation between the structural correlation length and the resistivity suggests that the microstructural disorder, generated by the dramatic mismatch between the NiCo2O4 and Al2O3 crystal structures, may be the origin of the absence of the metallic electrical transport in NiCo2O4. These results reveal microstructural disorder as another key factor in controlling the electrical transport of NiCo2O4, with potentially large magnetoresistance for spintronics application.
We demonstrate ultrafast magnetization dynamics in a 5d transition metal using circularly-polarized x-ray free electron laser in the hard x-ray region. A decay time of light-induced demagnetization of L1${}_0$-FePt was determined to be $tau_textrm{Pt
} = 0.6 textrm{ps}$ using time-resolved x-ray magnetic circular dichroism at the Pt L${}_3$ edge, whereas magneto-optical Kerr measurements indicated the decay time for total magnetization as $tau_textrm{total} = 0.1 textrm{ps}$. A transient magnetic state with the photo-modulated magnetic coupling between the 3d and 5d elements is firstly demonstrated.