Type-II Superconductivity below 4K in Sn0.4Sb0.6

228   0   0.0 ( 0 )
 نشر من قبل Veer Awana Dr
 تاريخ النشر 2020
  مجال البحث فيزياء
والبحث باللغة English




اسأل ChatGPT حول البحث

In this article, we report the occurrence of superconductivity in Sn0.4Sb0.6 single crystal at below 4K. Rietveld refined Powder XRD data confirms the phase purity of as grown crystal, crystallizing in rhombohedral R-3m space group with an elongated (2xc) unit cell in c-direction. Scanning Electron Microscope (SEM) image and EDAX measurement confirm the laminar growth and near to desired stoichiometry ratio. Raman Spectroscopy data shows the vibrational modes of Sn-Sb and Sb-Sb modes at 110 and 135cm-1. ZFC (Zero-Field-Cooled) magnetization measurements done at 10Oe showed sharp superconducting transitions at 4K along with a minor step at 3.5K. On the other hand, Paramagnetic Meissner Effect (PME) is observed in FC measurements. Magnetization vs applied field (M-H) plots at 2, 2.2, 2.5, 2.7, 3, 3.2, 3.5, and 3.7K shows typical Type-II nature of observed superconductivity with lower and upper critical fields (Hc1 and Hc2) at 69.42Oe and 630Oe respectively at 2K. Type-II superconductivity is also confirmed by calculated Ginzburg-Landau Kappa parameter value of 3.55. Characteristics length viz. coherence length and penetration depth are also calculated. Weak granular coupling is observed from R-T plot, in which resistance is not dropping to zero down to 2K.



قيم البحث

اقرأ أيضاً

We report synthesis of non-centrosymmetric BiPd single crystal by self flux method. The BiPd single crystal is crystallized in monoclinic structure with the P21 space group. Detailed SEM (Scanning Electron Microscopy) results show that the crystals a re formed in slab like morphology with homogenous distribution of Bi and Pd. The magnetic susceptibility measurement confirmed that the BiPd compound is superconducting below 4K. Further, BiPd exhibits weak ferromagnetism near the superconducting transition temperature in isothermal magnetization (MH) measurements. The temperature dependent electrical resistivity also confirmed that the BiPd single crystal is superconducting at Tc=4K. Magneto transport measurements showed that the estimated Hc2(0) value is around 7.0kOe. We also obtained a sharp peak in heat capacity Cp(T) measurements at below 4K due to superconducting ordering. The normalized specific-heat jump, DC/{gamma}Tc, is 1.52, suggesting the BiPd to be an intermediate BCS coupled superconductor. The pressure dependent electrical resistivity shows the Tc decreases with increasing applied pressure and the obtained dTc/dP is -0.62K/Gpa.
85 - W.M.Li , J.F.Zhao , L.P.Cao 2018
The mechanism of superconductivity in cuprates remains one of the big challenges of condensed matter physics.High Tc cuprates crystallize into layered perovskite structure featuring copper oxygen octahedral coordination. Due to the Jahn Teller effect in combination with the strong static Coulomb interaction, the octahedra in high Tc cuprates are elongated along the c axis, leading to a 3dx2-y2 orbital at the top of the band structure wherein the doped holes reside.This scenario gives rise to two dimensional characteristics in high Tc cuprates that favor d wave pairing symmetry. Here we report superconductivity in a cuprate Ba2CuO4-y wherein the local octahedron is in a very exceptional compressed version.The Ba2CuO4-y compound was synthesized at high pressure at high temperatures, and shows bulk superconductivity with critical temperature Tc above 70 K at ambient conditions. This superconducting transition temperature is more than 30 K higher than the Tc for the isostructural counterparts based on classical La2CuO4. X-ray absorption measurements indicate the heavily doped nature of the Ba2CuO4-y superconductor. In compressed octahedron the 3d3z2-r2 orbital will be lifted above the 3dx2-y2 orbital, leading to significant three dimensional nature in addition to the conventional 3dx2-y2 orbital. This work sheds important new light on advancing our comprehensive understanding of the superconducting mechanism of high Tc in cuprate materials.
The structure of the layered transition-metal Borides $A$B$_2$ ($A =$ Os, Ru) is built up by alternating $T$ and B layers with the B layers forming a puckered honeycomb. Here we report superconducting properties of RuB$_2$ with a $T_c approx 1.5$K us ing measurements of the magnetic susceptibility versus temperature $T$, magnetization $M$ versus magnetic field $H$, resistivity versus $T$, and heat capacity versus $T$ at various $H$. We observe a reduced heat capacity anomaly at $T_c$ given by $Delta C/gamma T_c approx 1.1$ suggesting multi-gap superconductivity. Strong support for this is obtained by the successful fitting of the electronic specific heat data to a two-gap model with gap values $Delta_1/k_BT_c approx 1.88$ and $Delta_2/k_BT_c approx 1.13$. Additionally, $M$ versus $H$ measurements reveal a behaviour consistent with Type-I superconductivity. This is confirmed by estimates of the Ginzburg-Landau parameter $kappa approx 0.1$--$0.66$. These results strongly suggest multi-gap Type-I superconductivity in RuB$_2$. We also calculate the band structure and obtain the Fermi surface for RuB$_2$. The Fermi surface consists of one quasi-two-dimensional sheet and two nested ellipsoidal sheets very similar to OsB$_2$. An additional small $4^{rm th}$ sheet is also found for RuB$_2$. RuB$_2$ could thus be a rare example of a multi-gap Type-I superconductor.
We grew the single crystals of the SnAs-based van der Waals (vdW)-type superconductor NaSn$_2$As$_2$ and systematically measured its resistivity, specific heat, and ultralow-temperature thermal conductivity. The superconducting transition temperature $T_c$ = 1.60 K of our single crystal is 0.3 K higher than that previously reported. A weak but intrinsic anomaly situated at 193 K is observed in both resistivity and specific heat, which likely arises from a charge-density-wave (CDW) instability. Ultralow-temperature thermal conductivity measurements reveal a fully-gapped superconducting state with a negligible residual linear term in zero magnetic field, and the field dependence of $kappa_0 / T$ further suggests NaSn$_2$As$_2$ is an $s$-wave superconductor.
Here we report the preparation and superconductivity of the 133-type Cr-based quasi-one-dimensional (Q1D) RbCr3As3 single crystals. The samples were prepared by the deintercalation of Rb+ ions from the 233-type Rb2Cr3As3 crystals which were grown fro m a high-temperature solution growth method. The RbCr3As3 compound crystallizes in a centrosymmetric structure with the space group of P63/m (No. 176) different with its non-centrosymmetric Rb2Cr3As3 superconducting precursor, and the refined lattice parameters are a = 9.373(3) {AA} and c = 4.203(7) {AA}. Electrical resistivity and magnetic susceptibility characterizations reveal the occurrence of superconductivity with an interestingly higher onset Tc of 7.3 K than other Cr-based superconductors, and a high upper critical field Hc2(0) near 70 T in this 133-type RbCr3As3 crystals.
التعليقات
جاري جلب التعليقات جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها
mircosoft-partner

هل ترغب بارسال اشعارات عن اخر التحديثات في شمرا-اكاديميا