تسجيل مستخدم جديدLattice dynamics and spin-phonon interaction in strained NiO films
317
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
NiO thin films with various strains were grown on SrTiO3 (STO) and MgO substrates using a pulsed laser deposition technique. The films were characterized using an x-ray diffractometer, atomic force microscopy, and infrared reflectance spectroscopy. The films grown on STO (001) substrate show a compressive in-plane strain which increases as the film thickness is reduced, resulting in an increase of the NiO phonon frequency. On the other hand, a tensile strain was detected in the NiO film grown on MgO (001) substrate which induces a softening of the phonon frequency. Overall, the variation of in-plane strain from -0.36% to +0.48% yields the decrease of the phonon frequency from 409.6 cm-1 to 377.5 cm-1 which occurs due to the ~1% change of the inter-atomic distances. The magnetic exchange -driven phonon splitting Delta(W) in three different sample, with relaxed (i.e. zero) strain, 0.36% compressive and 0.48% tensile strain was measured as a function of temperature. The Delta(W) increases on cooling in NiO relaxed film as in the previously published work on a bulk crystal. The splitting increases on cooling also in 0.48% tensile strained film, but Delta(W) is systematically 3-4 cm-1 smaller than in relaxed film. Since the phonon splitting is proportional to the non-dominant magnetic exchange interaction J1, the reduction of phonon splitting in tensile-strained film was explained by a diminishing J1 with lattice expansion. Increase of Delta(W) on cooling can be also explained by rising of J1 with reduced temperature.
قيم البحث
اقرأ أيضاً
Transition metal oxides possess complex free energy surfaces with competing degrees of freedom. Photoexcitation allows shaping of such rich energy landscapes. In epitaxially strained $mathrm{La_{0.67}Ca_{0.33}MnO_3}$, optical excitation with a sub-10
0 fs pulse above $2 mathrm{mJ/cm^2}$ leads to a persistent metallic phase below 100 K. Using single-shot optical and terahertz spectroscopy, we show that this phase transition is a multi-step process. We conclude that the phase transition is driven by partial charge order melting, followed by growth of the persistent metallic phase on longer timescales. A time-dependent Ginzburg-Landau model can describe the fast dynamics of the reflectivity, followed by longer timescale in-growth of the metallic phase.
We use femtosecond electron diffraction to study ultrafast lattice dynamics in the highly correlated antiferromagnetic (AF) semiconductor NiO. Using the scattering vector (Q) dependence of Bragg diffraction, we introduce a Q-resolved effective lattic
e temperature, and identify a nonthermal lattice state with preferential displacement of O compared to Ni ions, which occurs within ~0.3 ps and persists for 25 ps. We associate this with transient changes to the AF exchange striction-induced lattice distortion, supported by the observation of a transient Q-asymmetry of Friedel pairs. Our observation highlights the role of spin-lattice coupling in routes towards ultrafast control of spin order.
The lattice dynamics in Sr$_2$RuO$_4$ has been studied by inelastic neutron scattering combined with shell-model calculations. The in-plane bond-stretching modes in Sr$_2$RuO$_4$ exhibit a normal dispersion in contrast to all electronically doped per
ovskites studied so far. Evidence for strong electron phonon coupling is found for c-polarized phonons suggesting a close connection with the anomalous c-axis charge transport in Sr$_2$RuO$_4$.
MnO thin films with various thicknesses and strains were grown on MgO substrates by pulsed laser deposition, then characterized using x-ray diffraction and infrared reflectance spectroscopy. Films grown on (001)-oriented MgO substrates exhibit homoge
nous biaxial compressive strain which increases as the film thickness is reduced. For that reason, the frequency of doubly-degenerate phonon increases with the strain, and splits below Neel temperature TN due to the magnetic-exchange interaction. Films grown on (110)-oriented MgO substrates exhibit a huge phonon splitting already at room temperature due to the anisotropic in-plane compressive strain. Below TN, additional phonon is activated in the IR spectra; this trend is evidence for a spin-order-induced structural phase transition from tetragonal to monoclinic phase. Total phonon splitting is 55 cm-1 in (110)-oriented MnO film, which is more than twice the value in bulk MnO. This result is evidence that the nearest neighbor exchange interaction, which is responsible for the magnetically driven phonon splitting, is greatly increased in compressively strained films.
The dielectric properties of NiO thin films grown by pulsed laser deposition have been studied as a function of strain at temperature from 10 to 300 K. Above 150 K, the contribution of space-charge polarization to the dielectric permittivity of NiO f
ilms becomes dominant and the more defective films, which were grown at low temperatures show a drastical increase in the dielectric constant up to room temperature. While the atomically-ordered film, which was grown at high temperature doesnt show any considerable change in the dielectric constant in the range from 10 to 300 K. Below 100 K, the effect of strain on the dielectric constant becomes clear. An increase in dielectric permittivity is observed in the strained films while the relaxed film doesnt show any remarkable deviation from its bulk value. The low-temperature dielectric behavior of NiO thin film can be interpreted based on the effect of strain on the lattice dynamics of rocksalt binary oxides.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها