تسجيل مستخدم جديدEffect of sodium pyrophosphate and understanding microstructure of aqueous LAPONITE(R) dispersion using dissolution study
87
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
We investigate physical origin of ergodicity breaking in an aqueous colloidal dispersion of synthetic hectorite clay, LAPONITE(R), by performing dissolution and rheological experiments with monovalent salt and tetrasodium pyrophosphate solution. We also study the effect of interface, nitrogen and paraffin oil on the same. Dissolution experiments carried out for dispersions with both the interfaces show similar results. However, for samples with nitrogen interface, all the effects are observed to get expedited in time compared to paraffin oil interface. When kept in contact with water, 1.5 wt. % and 2.8 wt. % colloidal dispersion at pH 10 swell at small ages, while do not swell at large ages. The solution of tetrasodium pyrophosphate, interestingly, dissolves the entire colloidal dispersion samples with pH 10 irrespective of the clay concentration. Experiments carried out on colloidal dispersions prepared in water having pH 13 demonstrate no effect of water as well as sodium pyrophosphate solution on the same suggesting a possibility of the presence of negative charge on edge at that pH. We believe that all the behaviors observed for samples at pH 10 can be explained by an attractive gel microstructure formed by edge-to-face contact. Furthermore, the absence of swelling in old colloidal dispersion at pH 10 and dissolution of the same by sodium pyrophosphate solution cannot be explained by merely repulsive interactions. This behavior suggests that attractive interactions play an important role in causing ergodicity breaking in the colloidal dispersions at pH 10 at all the ages irrespective of the clay concentration. We substantiate the presence of fractal network structure formed by interparticle edge-face association using rheological tools and cryo-TEM imaging. We also conduct a comprehensive study of the effect of sodium pyrophosphate in the sol-gel transition of LAPONITE(R) dispersion.
قيم البحث
اقرأ أيضاً
Synthetic hectorite clay Laponite RD/XLG is composed of disk-shaped nanoparticles that acquire dissimilar charges when suspended in an aqueous media. Owing to their property to spontaneously self-assemble, Laponite is used as a rheology modifier in a
variety of commercial water-based products. Particularly, aqueous dispersion of Laponite undergoes liquid - to - solid transition at about 1 volume % concentration. The evolution of the physical properties as dispersion transforms to solid state is reminiscent of physical aging in molecular as well as colloidal glasses. The corresponding soft glassy dynamics of an aqueous Laponite dispersion, including the rheological behavior, has been extensively studied in the literature. In this feature article we take an overview of recent advances in understanding soft glassy dynamics and various efforts taken to understand the peculiar rheological behaviors. Furthermore, the continuously developing microstructure that is responsible for eventual formation of soft solid state that supports its own weight against gravity has also been a topic of intense debate and discussion. Particularly extensive experimental and theoretical studies lead to two types of microstructures for this system: an attractive gel-like or repulsive glass like. We carefully examine and critically analyze the literature and propose a state diagram that suggests aqueous Laponite dispersion to be present in an attractive gel state.
Aqueous suspensions of Laponite with discotic particles are well-studied and find a wide range of applications in industry. A new direction of their implementation is polymer composites that can exhibit improved physical properties.We have studied th
e aging of aqueous suspensions of Laponite and sodium polystyrene sulfonate (PSS-Na) and both their microscopic (small-angle X-ray scattering, SAXS) and macroscopic (small amplitude oscillatory shear (SAOS) rheometry) properties. The concentration of Laponite, $C_L$, was fixed at 2.5% wt and concentration of PSS-Na, $C_p$, was varied within 0-0.5% wt (0-24.2~mM). It is shown that the adding of PSS-Na significantly accelerates the aging.Nevertheless, the systems were stable against the sedimentation, and the flocculation didnt occur. Polyelectrolyte induced the appearance of large-scale fractal heterogeneities, which became more compact in the course of the aging. Polyelectrolyte induced the appearance of large-scale fractal heterogeneities, which became more compact in the course of the aging.
Na-montmorillonite is a natural clay mineral and is available in abundance in nature. The aqueous dispersions of charged and anisotropic platelets of this mineral exhibit non-ergodic kinetically arrested states ranging from soft glassy phases dominat
ed by interparticle repulsions to colloidal gels stabilized by salt induced attractive interactions. When the salt concentration in the dispersing medium is varied systematically, viscoelasticity and yield stress of the dispersion show non-monotonic behavior at a critical salt concentration, thus signifying a morphological change in the dispersion microstructures. We directly visualize the microscopic structures of these kinetically arrested phases using cryogenic scanning electron microscopy. We observe the existence of honeycomb-like network morphologies for a wide range of salt concentrations. The transition of the gel morphology, dominated by overlapping coin (OC) and house of cards (HoC) associations of clay particles at low salt concentrations to a new network structure dominated by face-face coagulation of platelets, is observed across the critical salt concentration. We further assess the stability of these gels under gravity using electroacoustics. This study, performed for concentrated clay dispersions for a wide concentration range of externally added salt, is useful in our understanding of many geophysical phenomena that involve the salt induced aggregation of natural clay minerals.
Investigating microstructure of suspensions with particles having anisotropic shape that share complex interactions is a challenging task leading to competing claims. This work investigates phase behavior of one such system: aqueous Laponite suspensi
on, which is highly contested in the literature, using rheological and microscopic tools. Remarkably, we observe that over a broad range of Laponite (1.4 to 4 weight %) and salt concentrations (0 to 7 mM), the system overwhelmingly demonstrates all the rheological characteristics of the sol-gel transition leading to a percolated network. Analysis of the rheological response leads to fractal dimension that primarily depends on the Laponite concentration. We also obtain the activation energy for gelation, which is observed to decrease with increase in Laponite as well as salt concentration. Significantly, the cryo-TEM images of the post-gel state clearly show presence of a percolated network formed by inter-particle bonds. The present work therefore conclusively establishes the system to be in an attractive gel state resolving a long-standing debate in the literature.
We use textit{ab initio} molecular dynamics simulations to investigate the properties of the dry surface of pure silica and sodium silicate glasses. The surface layers are defined based on the atomic distributions along the direction ($z-$direction)
perpendicular to the surfaces. We show that these surfaces have a higher concentration of dangling bonds as well as two-membered (2M) rings than the bulk samples. Increasing concentration of Na$_2$O reduces the proportion of structural defects. From the vibrational density of states, one concludes that 2M rings have a unique vibrational signature at a frequency $approx850$~cm$^{-1}$, compatible with experimental findings. We also find that, due to the presence of surfaces, the atomic vibration in the $z-$direction is softer than for the two other directions. The electronic density of states shows clear the differences between the surface and interior and we can attribute these to specific structural units. Finally, the analysis of the electron localization function allows to get insight on the influence of local structure and the presence of Na on the nature of chemical bonding in the glasses.