Self-powered sensors enabled by wide-bandgap perovskite indoor photovoltaic cells

86   0   0.0 ( 0 )
 نشر من قبل Ian Mathews Dr
 تاريخ النشر 2019
والبحث باللغة English




اسأل ChatGPT حول البحث

We present a new approach to ubiquitous sensing for indoor applications, using high-efficiency and low-cost indoor perovksite photovoltaic cells as external power sources for backscatter sensors. We demonstrate wide-bandgap perovskite photovoltaic cells for indoor light energy harvesting with the 1.63eV and 1.84 eV devices demonstrate efficiencies of 21% and 18.5% respectively under indoor compact fluorescent lighting, with a champion open-circuit voltage of 0.95 V in a 1.84 eV cell under a light intensity of 0.16 mW/cm2. Subsequently, we demonstrate a wireless temperature sensor self-powered by a perovskite indoor light-harvesting module. We connect three perovskite photovoltaic cells in series to create a module that produces 14.5 uW output power under 0.16 mW/cm2 of compact fluorescent illumination with an efficiency of 13.2%. We use this module as an external power source for a battery-assisted RFID temperature sensor and demonstrate a read range by of 5.1 meters while maintaining very high frequency measurements every 1.24 seconds. Our combined indoor perovskite photovoltaic modules and backscatter radio-frequency sensors are further discussed as a route to ubiquitous sensing in buildings given their potential to be manufactured in an integrated manner at very low-cost, their lack of a need for battery replacement and the high frequency data collection possible.

قيم البحث

اقرأ أيضاً

The self-powered sensing system could harness ambient energy to power the sensor without the need for external electrical energy. Recently, the concept of photovoltaic (PV) self-powered gas sensing has aroused wider attentions due to room-temperature operation, low power consumption, small size and potential applications. The PV self-powered gas sensors integrate the photovoltaic effects and the gas sensing function into a single chip, which could truly achieve the goal of zero power consumption for an independent gas sensing device. As an emerging concept, the PV self-powered gas sensing has been achieved by using different strategies, including integrated gas sensor and solar cell, integrated light filter and solar cell, gas-sensitive heterojunction photovoltaics, and gas-sensitive lateral photovoltaics, respectively. The purpose of this review is to summarize recent advances of PV self-powered gas sensing and also remark on the directions for future research in this topic.
Photovoltaic (PV) cells have the potential to serve as on-board power sources for low-power IoT devices. Here, we explore the use of perovskite solar cells to power Radio Frequency (RF) backscatter-based IoT devices with a few {mu}W power demand. Per ovskites are suitable for low-cost, high-performance, low-temperature processing, and flexible light energy harvesting that hold the possibility to significantly extend the range and lifetime of current backscatter techniques such as Radio Frequency Identification (RFID). For these reasons, perovskite solar cells are prominent candidates for future low-power wireless applications. We report on realizing a functional perovskite-powered wireless temperature sensor with 4 m communication range. We use a 10.1% efficient perovskite PV module generating an output voltage of 4.3 V with an active area of 1.06 cm2 under 1 sun illumination, with AM 1.5G spectrum, to power a commercial off-the-shelf RFID IC, requiring 10 - 45 {mu}W of power. Having an on-board energy harvester provides extra-energy to boost the range of the sensor (5x) in addition to providing energy to carry out high-volume sensor measurements (hundreds of measurements per min). Our evaluation of the prototype suggests that perovskite photovoltaic cells are able to meet the energy needs to enable fully autonomous low-power RF backscatter applications of the future. We conclude with an outlook into a range of applications that we envision to leverage the synergies offered by combining perovskite photovoltaics and RFID.
The power conversion efficiency of an ultrathin CIGS solar cell was maximized using a coupled optoelectronic model to determine the optimal bandgap grading of the nonhomogeneous CIGS layer in the thickness direction. The bandgap of the CIGS layer was either sinusoidally or linearly graded, and the solar cell was modeled to have a metallic backreflector corrugated periodically along a fixed direction in the plane. The model predicts that specially tailored bandgap grading can significantly improve the efficiency, with much smaller improvements due to the periodic corrugations. An efficiency of 27.7% with the conventional 2200-nm-thick CIGS layer is predicted with sinusoidal bandgap grading, in comparison to 22% efficiency obtained experimentally with homogeneous bandgap. Furthermore, the inclusion of sinusoidal grading increases the predicted efficiency to 22.89% with just a 600-nm-thick CIGS layer. These high efficiencies arise due to a large electron-hole-pair generation rate in the narrow-bandgap regions and the elevation of the open-circuit voltage due to a wider bandgap in the region toward the front surface of the CIGS layer. Thus, bandgap nonhomogeneity, in conjunction with periodic corrugation of the backreflector, can be effective in realizing ultrathin CIGS solar cells that can help overcome the scarcity of indium.
We explore the degradation behaviour under continuous illumination and direct oxygen exposure of inverted unencapsulated formamidinium(FA)0.83Cs0.17Pb(I0.8Br0.2)3, CH3NH3PbI3, and CH3NH3PbI3-xClx perovskite solar cells. We continuously test the devic es in-situ and in-operando with current-voltage sweeps, transient photocurrent, and transient photovoltage measurements, and find that degradation in the CH3NH3PbI3-xClx solar cells due to oxygen exposure occurs over shorter timescales than FA0.83Cs0.17Pb(I0.8Br0.2)3 mixed-cation devices. We attribute these oxygen-induced losses in the power conversion efficiencies to the formation of electron traps within the perovskite photoactive layer. Our results highlight that the formamidinium-caesium mixed-cation perovskites are much less sensitive to oxygen-induced degradation than the methylammonium-based perovskite cells, and that further improvements in perovskite solar cell stability should focus on the mitigation of trap generation during ageing.
An optoelectronic optimization was carried out for an AlGaAs solar cell containing (i) an n-AlGaAs absorber layer with a graded bandgap and (ii) a periodically corrugated Ag backreflector combined with localized ohmic Pd-Ge-Au backcontacts. The bandg ap of the absorber layer was varied either sinusoidally or linearly. An efficiency of 33.1% with the 2000-nm-thick n-AlGaAs absorber layer is predicted with linearly graded bandgap along with silver backreflector and localized ohmic backcontacts, in comparison to 27.4% efficiency obtained with homogeneous bandgap and a continuous ohmic backcontact. Sinusoidal grading of the bandgap {is predicted to enhance} the maximum efficiency to 34.5%. Thus, grading the bandgap of the absorber layer, along with a periodically corrugated Ag backreflector and localized ohmic Pd-Ge-Au backcontacts can help realize ultrathin and high-efficient AlGaAs solar cells for terrestrial applications.
التعليقات
جاري جلب التعليقات جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها
mircosoft-partner

هل ترغب بارسال اشعارات عن اخر التحديثات في شمرا-اكاديميا