We investigate the origin of the hysteresis observed in the transfer characteristics of back-gated field-effect transistors with an exfoliated MoS2 channel. We find that the hysteresis is strongly enhanced by increasing either gate voltage, pressure, temperature or light intensity. Our measurements reveal a step-like behavior of the hysteresis around room temperature, which we explain as water-facilitated charge trapping at the MoS2/SiO2 interface. We conclude that intrinsic defects in MoS2, such as S vacancies, which result in effective positive charge trapping, play an important role, besides H2O and O2 adsorbates on the unpassivated device surface. We show that the bistability associated to the hysteresis can be exploited in memory devices.
قيم البحث
اقرأ أيضاً
The so-called Boltzmann Tyranny defines the fundamental thermionic limit of the subthreshold slope (SS) of a metal-oxide-semiconductor field-effect transistor (MOSFET) at 60 mV/dec at room temperature and, therefore, precludes the lowering of the sup
ply voltage and the overall power consumption. Adding a ferroelectric negative capacitor to the gate stack of a MOSFET may offer a promising solution to bypassing this fundamental barrier. Meanwhile, two-dimensional (2D) semiconductors, such as atomically thin transition metal dichalcogenides (TMDs) due to their low dielectric constant, and ease of integration in a junctionless transistor topology, offer enhanced electrostatic control of the channel. Here, we combine these two advantages and demonstrate for the first time a molybdenum disulfide (MoS2) 2D steep slope transistor with a ferroelectric hafnium zirconium oxide layer (HZO) in the gate dielectric stack. This device exhibits excellent performance in both on- and off-states, with maximum drain current of 510 {mu}A/{mu}m, sub-thermionic subthreshold slope and is essentially hysteresis-free. Negative differential resistance (NDR) was observed at room temperature in the MoS2 negative capacitance field-effect-transistors (NC-FETs) as the result of negative capacitance due to the negative drain-induced-barrier-lowering (DIBL). High on-current induced self-heating effect was also observed and studied.
We discuss the high-bias electrical characteristics of back-gated field-effect transistors with CVD-synthesized bilayer MoS2 channel and Ti Schottky contacts. We find that oxidized Ti contacts on MoS2 form rectifying junctions with ~0.3 to 0.5 eV Sch
ottky barrier height. To explain the rectifying output characteristics of the transistors, we propose a model based on two slightly asymmetric back-to-back Schottky barriers, where the highest current arises from image force barrier lowering at the electrically forced junction, while the reverse current is due to Schottky-barrier limited injection at the grounded junction. The device achieves a photo responsivity greater than 2.5 AW-1 under 5 mWcm-2 white-LED light. By comparing two- and four-probe measurements, we demonstrate that the hysteresis and persistent photoconductivity exhibited by the transistor are peculiarities of the MoS2 channel rather than effects of the Ti/MoS2 interface.
Monolayer transition metal dichalcogenides (TMD) have numerous potential applications in ultrathin electronics and photonics. The exposure of TMD based devices to light generates photo-carriers resulting in an enhanced conductivity, which can be effe
ctively used, e.g., in photodetectors. If the photo-enhanced conductivity persists after removal of the irradiation, the effect is known as persistent photoconductivity (PPC). Here we show that ultraviolet light (wavelength = 365 nm) exposure induces an extremely long-living giant PPC (GPPC) in monolayer MoS2 (ML-MoS2) field-effect transistors (FET) with a time constant of ~30 days. Furthermore, this effect leads to a large enhancement of the conductivity up to a factor of 107. In contrast to previous studies in which the origin of the PPC was attributed to extrinsic reasons such as trapped charges in the substrate or adsorbates, we unambiguously show that the GPPC arises mainly from the intrinsic properties of ML-MoS2 such as lattice defects that induce a large amount of localized states in the forbidden gap. This finding is supported by a detailed experimental and theoretical study of the electric transport in TMD based FETs as well as by characterization of ML-MoS2 with scanning tunneling spectroscopy, high-resolution transmission electron microscopy, and photoluminescence measurements. The obtained results provide a basis towards the defect-based engineering of the electronic and optical properties of TMDs for device applications.
Recent discoveries of the photoresponse of molybdenum disulfide (MoS2) have shown the considerable potential of these two-dimensional transition metal dichalcogenides for optoelectronic applications. Among the various types of photoresponses of MoS2,
persistent photoconductivity (PPC) at different levels has been reported. However, a detailed study of the PPC effect and its mechanism in MoS2 is still not available, despite the importance of this effect on the photoresponse of the material. Here, we present a systematic study of the PPC effect in monolayer MoS2 and conclude that the effect can be attributed to random localized potential fluctuations in the devices. Notably, the potential fluctuations originate from extrinsic sources based on the substrate effect of the PPC. Moreover, we point out a correlation between the PPC effect in MoS2 and the percolation transport behavior of MoS2. We demonstrate a unique and efficient means of controlling the PPC effect in monolayer MoS2, which may offer novel functionalities for MoS2-based optoelectronic applications in the future.
We report on the fabrication and characterization of synthesized multiwall MoS2 nanotube (NT) and nanoribbon (NR) field-effect transistors (FETs). The MoS2 NTs and NRs were grown by chemical transport, using iodine as a transport agent. Raman spectro
scopy confirms the material as unambiguously MoS2 in NT, NR, and flake forms. Transmission electron microscopy was used to observe cross sections of the devices after electrical measurements and these were used in the interpretation of the electrical measurements allowing estimation of the current density. The NT and NR FETs demonstrate n-type behavior, with ON/OFF current ratios exceeding 10^3, and with current densities of 1.02 {mu}A/{mu}m, and 0.79 {mu}A/{mu}m at VDS = 0.3 V and VBG = 1 V, respectively. Photocurrent measurements conducted on a MoS2 NT FET, revealed short-circuit photocurrent of tens of nanoamps under an excitation optical power of 78 {mu}W and 488 nm wavelength, which corresponds to a responsivity of 460 {mu}A/W. A long channel transistor model was used to model the common-source characteristics of MoS2 NT and NR FETs and was shown to be consistent with the measured data.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها