تسجيل مستخدم جديدCharacterisations of ohmic and Schottky contacts of a single ZnO nanowire
111
0
0.0
(
0
)
تأليف
B. Bercu
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
Current voltage and Kelvin Probe Force Microscopy (KPFM) measurements were performed on single ZnO nanowires. Measurements are shown to be strongly correlated with the contact behavior, either ohmic or Schottky. The ZnO nanowires were obtained by metallo-organic chemical vapor deposition (MOCVD) and contacted using electronic-beam lithography. Depending on the contact geometry, good quality ohmic contacts (linear I V behavior) or non-linear (diode like) Schottky contacts were obtained. Current voltage and KPFM measurements on both types of contacted ZnO nanowires were performed in order to investigate their behavior. A clear correlation could be established between the I V curve, the electrical potential profile along the device and the nanowire geometry. Some arguments supporting this behavior are given based on a depleted region extension. This work will help to better understand the electrical behavior of ohmic contacts on single ZnO nanowires, for future applications in nanoscale field effect-transistors and nano-photodetectors.
قيم البحث
اقرأ أيضاً
The 2D ferromagnets, such as CrX3 (X=Cl, Br and I), have been attracting extensive attentions since they provide novel platforms to fundamental physics and device applications. Integrating CrX3 with other electrodes and substrates is an essential ste
p to their device realization. Therefore, it is important to understand the interfacial properties between CrX3 and other 2D materials. As an illustrative example, we have investigated the heterostructures between CrX3 and graphene (CrX3/Gr) from firstprinciples. We find unique Schottky contacts type with strongly spin-dependent barriers in CrX3/Gr. This can be understood by synergistic effects between the exchange splitting of semiconductor band of CrX3 and interlayer charge transfer. The spinasymmetry of Schottky barriers may result in different tunneling rates of spin-up and down electrons, and then lead to spin-polarized current, namely spin-filter (SF) effect. Moreover, by introducing X vacancy into CrX3/Gr, an Ohmic contact forms in spin-up direction. It may enhance the transport of spin-up electrons, and improve SF effect. Our systematic study reveals the unique interfacial properties of CrX3/Gr, and provides a theoretical view to the understanding and designing of spintronics device based on magnetic vdW heterostructures.
Long needle-shaped single crystals of Zn1-xCoxO were grown at low temperatures using a molten salt solvent technique, up to x=0.10. The conduction process at low temperatures is determined to be by Mott variable range hopping. Both pristine and cobal
t doped crystals clearly exhibit a crossover from negative to positive magnetoresistance as the temperature is decreased. The positive magnetoresistance of the Zn1-xCoxO single crystals increases with increased Co concentration and reaches up to 20% at low temperatures (2.5 K) and high fields (>1 T). SQUID magnetometry confirms that the Zn1-xCoxO crystals are predominantly paramagnetic in nature and the magnetic response is independent of Co concentration. The results indicate that cobalt doping of single crystalline ZnO introduces localized electronic states and isolated Co2+ ions into the host matrix, but that the magnetotransport and magnetic properties are decoupled.
Optimum design of efficient nanowire solar cells requires better understanding of light diffusion in a nanowire array. Here we demonstrate that our recently developed ultrafast all-optical shutter can be used to directly measure the dwell time of lig
ht in a nanowire array. Our measurements on disordered ZnO nanowire arrays, nanowire forests, indicate that the photon mean free path and the dwell time of light can be well predicted from SEM images.
Semiconductor nanowires (NWs) have a broad range of applications for nano- and optoelectronics. The strain field of gallium nitride (GaN) NWs could be significantly changed when contacts are applied to them to form a final device, especially consider
ing the piezoelectric properties of GaN. Investigation of influence of the metallic contacts on the structure of the NWs is of high importance for their applications in real devices. We have studied a series of different type of contacts and influence of the applied voltage bias on the contacted GaN NWs with the length of about 3 to 4 micrometers and with two different diameters of 200 nm and 350 nm. It was demonstrated that the NWs with the diameter of 200 nm are bend already by the interaction with the substrate. For all GaN NWs, significant structural changes were revealed after the contacts deposition. The results of our research may contribute to the future optoelectronic applications of the GaN nanowires.
The electrical and photodiode characteristics of ensemble and single p-GaN nanowire and n-Si heterojunction devices were studied. Ideality factor of the single nanowire p-GaN/n-Si device was found to be about three times lower compared to that of the
ensemble nanowire device. Apart from the deep-level traps in p-GaN nanowires, defect states due to inhomogeneity in Mg dopants in the ensemble nanowire device are attributed to the origin of high ideality factor. Photovoltaic mode of ensemble nanowire device showed an improvement in the fill-factors up to 60 percent over the single nanowire device with fill-factors up to 30 percent. Reponsivity of the single nanowire device in photoconducting mode was found to be enhanced by five orders, at 470 nm. The enhanced photoresponse of the single nanowire device also confirms the photoconduction due to defect states in p-GaN nanowires.