Optomechanical devices sensitively transduce and actuate motion of nanomechanical structures using light. Single--crystal diamond promises to improve the performance of optomechanical devices, while also providing opportunities to interface nanomechanics with diamond color center spins and related quantum technologies. Here we demonstrate dissipative waveguide--optomechanical coupling exceeding 35 GHz/nm to diamond nanobeams supporting both optical waveguide modes and mechanical resonances, and use this optomechanical coupling to measure nanobeam displacement with a sensitivity of $9.5$ fm/$sqrt{text{Hz}}$ and optical bandwidth $>150$nm. The nanobeams are fabricated from bulk optical grade single--crystal diamond using a scalable undercut etching process, and support mechanical resonances with quality factor $2.5 times 10^5$ at room temperature, and $7.2 times 10^5$ in cryogenic conditions (5K). Mechanical self--oscillations, resulting from interplay between photothermal and optomechanical effects, are observed with amplitude exceeding 200 nm for sub-$mu$W absorbed optical power, demonstrating the potential for optomechanical excitation and manipulation of diamond nanomechanical structures.
Single-crystal diamond cavity optomechanical devices are a promising example of a hybrid quantum system: by coupling mechanical resonances to both light and electron spins, they can enable new ways for photons to control solid state qubits. However,
We study the photocurrent induced by pulsed-light illumination (pulse duration is several nanoseconds) of single-crystal diamond containing nitrogen impurities. Application of additional continuous-wave light of the same wavelength quenches pulsed ph
Diamond is a material of choice in the pursuit of integrated quantum photonic technologies. So far, the majority of photonic devices fabricated from diamond, are made from (100)-oriented crystals. In this work, we demonstrate a methodology for the fa
Single crystal diamond membranes that host optically active emitters are highly attractive components for integrated quantum nanophotonics. In this work we demonstrate bottom-up synthesis of single crystal diamond membranes containing the germanium v
Observation of the Fano line shapes is essential to understand properties of the Fano resonance in different physical systems. We explore a tunable Fano resonance by tuning the phase shift in a Mach-Zehnder interferometer (MZI) based on a single-mode