We report the interplay between In incorporation and strain relaxation kinetics in high-In-content InxGa1-xN (x = 0.3) layers grown by plasma-assisted molecular-beam epitaxy. For In mole fractions x = 0.13-0.48, best structural and morphological quality is obtained under In excess conditions, at In accumulation limit, and at a growth temperature where InGaN decomposition is active. Under such conditions, in situ and ex situ analysis of the evolution of the crystalline structure with the growth thickness points to an onset of misfit relaxation after the growth of 40 nm, and a gradual relaxation during more than 200 nm which results in an inhomogeneous strain distribution along the growth axis. This process is associated with a compositional pulling effect, i.e. indium incorporation is partially inhibited in presence of compressive strain, resulting in a compositional gradient with increasing In mole fraction towards the surface.
High-index Bi2Se3(221) film has been grown on In2Se3-buffered GaAs(001), in which a much retarded strain relaxation dynamics is recorded. The slow strain-relaxation process of in epitaxial Bi2Se3(221) can be attributed to the layered structure of Bi2
The Pd, and Pt based ABO2 delafossites are a unique class of layered, triangular oxides with 2D electronic structure and a large conductivity that rivals the noble metals. Here, we report successful growth of the metallic delafossite PdCoO2 by molecu
The growth of single layer graphene nanometer size domains by solid carbon source molecular beam epitaxy on hexagonal boron nitride (h-BN) flakes is demonstrated. Formation of single-layer graphene is clearly apparent in Raman spectra which display s
We have investigated the growth of BaTiO3 thin films deposited on pure and 1% Nb-doped SrTiO3(001) single crystals using atomic oxygen assisted molecular beam epitaxy (AO-MBE) and dedicated Ba and Ti Knudsen cells. Thicknesses up to 30 nm were invest
We report on the growth of epitaxial Sr2RuO4 films using a hybrid molecular beam epitaxy approach in which a volatile precursor containing RuO4 is used to supply ruthenium and oxygen. The use of the precursor overcomes a number of issues encountered