تسجيل مستخدم جديد(Sr3La2O5)(Zn1-xMnx)2As2: A Bulk Form Diluted Magnetic Semiconductor isostructural to the 32522 Fe-based Superconductors
138
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
A new diluted magnetic semiconductor system, (Sr3La2O5)(Zn1-xMnx)2As2, has been synthesized and characterized. 10% Mn substitution for Zn in bulk form (Sr3La2O5)Zn2As2 results in a ferromagnetic ordering below Curie temperature, TC ~ 40 K. (Sr3La2O5)(Zn1-xMnx)2As2 has a layered crystal structure identical to that of 32522-type Fe based superconductors, and represents the fifth DMS family that has a direct counterpart among the FeAs high temperature superconductor families.
قيم البحث
اقرأ أيضاً
We report the synthesis and characterization of a bulk diluted magnetic semiconductor (La1-xBax)(Zn1-xMnx)AsO (0 <= x <= 0.2) with a layered crystal structure identical to that of the 1111 FeAs superconductors. No ferromagnetic order occurs for (Zn,M
n) substitution in the parent compound LaZnAsO without charge doping. Together with carrier doping via (La,Ba) sub- stitution, a small amount of Mn substituting for Zn results in ferromagnetic order with TC up to ~40 K, although the system remains semiconducting. Muon spin relaxation measurements confirm the development of ferromagnetic order in the entire volume, with the relationship between the internal field and TC consistent with the trend found in (Ga,Mn)As, the 111 Li(Zn,Mn)As, and the 122 (Ba,K)(Zn,Mn)2As2 systems.
We report the synthesis and characterization of bulk form diluted magnetic semiconductors Ba(Zn1-2xMnxCox)2As2 (0 <= x <= 0.15) with a crystal structure identical to that of 122-type Fe-based superconductors. Mn and Co co-doping into the parent compo
und BaZn2As2 results in a ferromagnetic ordering below TC ~ 80 K. Hall effect measurements indicate that the carrier are n-type with the density of ~10^17/cm3. The common crystal structure and excellent lattice matching between the p-type ferromagnetic (Ba1-yKy)(Zn1-xMnx)2As2, the n-type ferromagnetic Ba(Zn1-2xMnxCox)2As2, the antiferrmagnetic BaMn2As2 and the superconducting Ba(Fe1-xCox)2As2 systems make it possible to make various junctions between these systems through the As layer.
We report the synthesis and characterization of bulk form diluted magnetic semiconductors I-II-V Li1.1(Zn1-xCrx)As (x = 0.03, 0.05, 0.10, 0.15)with a cubic crystal structure identical to that of III-V GaAs and II-VI zinc-blende ZnSe. With p-type carr
iers created by excess Li, 10% Cr substitution for Zn results in a ferromagnetic ordering below TC ~ 218 K. Li(Zn,Cr)As represents another magnetic semiconducting system with the advantage of decoupling carriers and spins, where carriers are created by adding extra Li and spins are introduced by Cr substitution for Zn.
The doping effect of Sr and transition metals Mn, Fe, Co into the direct-gap semiconductor LaZnAsO has been investigated. Our results indicate that the single phase ZrCuSiAs-type tetragonal crystal structure is preserved in (La1-xSrx)(Zn1-xTMx)AsO (T
M = Mn, Fe, Co) with the doping level up to x = 0.1. While the system remains semiconducting, doping with Sr and Mn results in ferromagnetic order with TC ~ 30K, and doping with Sr and Fe results in a spin glass like state below ~6K with a saturation moment of ~0.02 muB/Fe, an order of magnitude smaller than the ~0.4 muB/Mn of Sr and Mn doped samples. The same type of magnetic state is observed neither for (Zn,Fe) substitution without carrier doping, nor for Sr and Co doped specimens.
We use muon spin relaxation (muSR) to investigate the magnetic properties of a bulk form diluted ferromagnetic semiconductor (DFS) Li1.15(Zn0.9Mn0.1)P with T_C ~ 22 K. MuSR results confirm the gradual development of ferromagnetic ordering below T_C w
ith a nearly 100% magnetic ordered volume. Despite its low carrier density, the relation between static internal field and Curie temperature observed for Li(Zn,Mn)P is consistent with the trend found in (Ga,Mn)As and other bulk DFSs, indicating these systems share a common mechanism for the ferromagnetic exchange interaction. Li1+y(Zn1-xMnx)P has the advantage of decoupled carrier and spin doping, where Mn2+ substitution for Zn2+ introduces spins and Li+ off-stoichiometry provides carriers. This advantage enables us to investigate the influence of overdoped Li on the ferromagnetic ordered state. Overdoping Li suppresses both T_C and saturation moments for a certain amount of spins, which indicates that more carriers are detrimental to the ferromagnetic exchange interaction, and that a delicate balance between charge and spin densities is required to achieve highest T_C.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها