We present experimental XMLD spectra measured on epitaxial (001)-oriented thin Co$_{2}$FeSi films, which are rich in features and depend sensitively on the degree of atomic order and interdiffusion from capping layers. Al- and Cr-capped films with different degrees of atomic order were prepared by DC magnetron sputtering by varying the deposition temperatures. The local structural properties of the film samples were additionally investigated by nuclear magnetic resonance (NMR) measurements. The XMLD spectra of the different samples show clear and uniform trends at the $L_{3,2}$ edges. The Al-capped samples show similar behavior as previous measured XMLD spectra of Co$_2$FeSi$_{0.6}$Al$_{0.4}$. Thus, we assume that during deposition Al atoms are being implanted into the subsurface of Co$_{2}$FeSi. Such an interdiffusion is not observed for the corresponding Cr-capped films, which makes Cr the material of choice for capping Co$_{2}$FeSi films. We report stronger XMLD intensities at the $L_{3,2}$ Co and Fe egdes for films with a higher saturation magnetization. Additionally, we compare the spectra with textit{ab initio} predictions and obtain a reasonably good agreement. Furthermore, we were able to detect an XMCD signal at the Si $L$-edge, indicating the presence of a magnetic moment at the Si atoms.
We investigate the magnetic and electronic properties of the Gd$T_2$Zn$_{20}$ ($T$ = Fe and Co) compounds using X-ray resonant magnetic scattering (XRMS), X-ray absorption near-edge structure (XANES) and X-ray magnetic circular dichroism (XMCD) techn
We have studied the electronic and magnetic states of Co and Mn atoms at the interface of the Co$_mathrm{2}$Mn$_{beta}$Si (CMS)/MgO ($beta$=0.69, 0.99, 1.15 and 1.29) magnetic tunnel junction (MTJ) by means of x-ray magnetic circular dichroism. In pa
We report on the results of x-ray absorption (XAS), x-ray magnetic circular dichroism (XMCD), and photoemission experiments on {it n}-type Zn$_{1-x}$Co$_x$O ($x=0.05$) thin film, which shows ferromagnetism at room temperature. The XMCD spectra show a
We report the deposition of thin Co$_2$FeSi films by RF magnetron sputtering. Epitaxial (100)-oriented and L2$_1$ ordered growth is observed for films grown on MgO(100) substrates. (110)-oriented films on Al$_2$O$_3$(110) show several epitaxial domai
The X-ray magnetic circular dichroism (XMCD) has been measured at the Co K edge in Co-hcp and R-Co compounds (R=La, Tb, Dy). The structure of the experimental XMCD spectra in the near-edge region has been observed to be highly sensitive to the magnet