We obtained amorphous-FeAs-free SmFeAsO1-xFx using a low temperature sintering with slow cooling. SmFeAsO1-xFx is sintered at 980 {deg}C for 40 hours and cooled slowly down to 600 {deg}C. The low temperature sintering suppresses the formation of amorphous FeAs, and the slow cooling introduces much fluorine into SmFeAsO1-xFx. The superconductivity of this sample appears at 57.8 K and the superconducting volume fraction reaches 96 %. To study the change of fluorine concentration during the cooling process, samples are quenched by water at 950 {deg}C, 900 {deg}C, 850 {deg}C, 800 {deg}C, 750 {deg}C and 700 {deg}C. It is found that fluorine is substituted not only at the maximum heating temperature but also during the cooling process. The low temperature sintering with slow cooling is very effective to obtain a homogeneous SmFeAsO1-xFx with high fluorine concentration.
قيم البحث
اقرأ أيضاً
The Phase diagram of SmFeAsO1-xFx in terms of x is exhibited in this study. SmFeAsO1-xFx from x = 0 to x = 0.3 were prepared by low temperature sintering with slow cooling. The low temperature sintering suppresses the formation of the amorphous FeAs,
which is inevitably produced as an impurity by using high temperature sintering. Moreover, slow cooling is effective to obtain the high fluorine concentration. The compositional change from feedstock composition is quite small after this synthesis. We can reproducibly observe a record superconducting transition for an iron based superconductor at 58.1 K. This achievement of a high superconducting transition is due to the success in a large amount of fluorine substitution. A shrinking of the a lattice parameter caused by fluorine substitution is observed and the substitutional rate of fluorine changes at x =0.16.
We have studied the structural and electronic phase diagrams of CeFeAsO1-xFx and SmFeAsO1-xFx by a detailed analysis of muon spin relaxation experiments, synchrotron X-ray diffraction, Mossbauer spectroscopy, electrical resistivity, specific heat, an
d magnetic susceptibility measurements (Full abstract in the main document).
The recent observation of superconductivity with critical temperatures up to 55 K in the FeAs based pnictide compounds marks the first discovery of a non copper-oxide based layered high-Tc superconductor (HTSC) [1-3]. It has raised the suspicion that
these new materials share a similar pairing mechanism to the cuprates, since both exhibit superconductivity following charge doping of a magnetic parent material. Here we present a muon spin rotation study on SmFeAsO1-xFx (x=0-0.30), which shows that static magnetism persists well into the superconducting regime. The analogy with the cuprates is quite surprising since the parent compounds appear to have different magnetic ground states: itinerant spin density wave for the pnictides contrasted with the Mott-Hubbard insulator in the cuprates. Our findings suggest that proximity to magnetic order and associated soft magnetic fluctuations, rather than the strong electronic correlations in the vicinity of a Mott-Hubbard-metal-to-insulator transition, may be the key ingredients of HTSC.
The recent discovery of superconductivity in oxypnictides with the critical temperature (TC) higher than McMillan limit of 39 K (the theoretical maximum predicted by Bardeen-Cooper-Schrieffer (BCS) theory) has generated great excitement. Theoretical
calculations indicate that the electron-phonon interaction is not strong enough to give rise to such high transition temperatures, while strong ferromagnetic/antiferromagnetic fluctuations have been proposed to be responsible. However, superconductivity and magnetism in pnictide superconductors show a strong sensitivity to the lattice, suggesting a possibility of unconventional electron-phonon coupling. Here we report the effect of oxygen and iron isotopic mass on Tc and the spin-density wave (SDW) transition temperature (TSDW) in SmFeAsO1-xFx and Ba1-xKxFe2As2 systems. The results show that oxygen isotope effect on TC and TSDW is very little, while the iron isotope exponent alpha=-dlnTc/dlnM is about 0.35, being comparable to 0.5 for the full isotope effect. Surprisingly, the iron isotope exchange shows the same effect on TSDW as TCc These results indicate that electron-phonon interaction plays some role in the superconducting mechanism, but simple electron-phonon coupling mechanism seems to be rather unlikely because a strong magnon-phonon coupling is included. Sorting out the interplay between the lattice and magnetic degrees of freedom is a key challenge for understanding the mechanism of high-TC superconductivity.
SmFeAsO1-xFx tapes were prepared using three kinds of starting materials. It shows that the starting materials have an obvious effect on the impurity phases in final superconducting tapes. Compared with the other samples, the samples fabricated by Sm
As, FeO, Fe2As, and SmF3 have the smallest arsenide impurity phase and voids. As a result, these samples possess much denser structure and better grain connectivity. Moreover, among the three kinds of samples fabricated in this work, this kind of sample has the highest zero-resistivity temperature ~40 K and largest critical current density ~4600 A/cm^2 in self-field at 4.2 K. This is the highest Jc values reported so far for SmFeAsO1-xFx wires and tapes.