تسجيل مستخدم جديدTransport properties and the anisotropy of Ba_{1-x}K_xFe_2As_2 single crystals in normal and superconducting states
67
0
0.0
(
0
)
تأليف
V.N. Zverev
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
The transport and superconducting properties of Ba_{1-x}K_xFe_2As_2 single crystals with T_c = 31 K were studied. Both in-plane and out-of plane resistivity was measured by modified Montgomery method. The in-plane resistivity for all studied samples, obtained in the course of the same synthesis, is almost the same, unlike to the out-of plane resistivity, which differ considerably. We have found that the resistivity anisotropy gamma=rho_c /rho_{ab} is almost temperature independent and lies in the range 10-30 for different samples. This, probably, indicates on the extrinsic nature of high out-of-plane resistivity, which may appear due to the presence of the flat defects along Fe-As layers in the samples. This statement is supported by comparatively small effective mass anisotropy, obtained from the upper critical field measurements, and from the observation of the so-called Friedel transition, which indicates on the existence of some disorder in the samples in c-direction.
قيم البحث
اقرأ أيضاً
We report on isofield magnetization curves obtained as a function of temperature in two single crystals of $Ba_{1-x}K_xFe_2As_2$ with superconducting transition temperature $T_c$=28K and 32.7 K. Results obtained for fields above 20 kOe show a well de
fined rounding effect on the reversible region extending 1-3 K above $T_c(H)$ masking the transition. This rounding appears to be due to three-dimensional critical fluctuations, as the higher field curves obey a well know scaling law for this type of critical fluctuations. We also analysed the asymptotic behavior of $sqrt M$vs.T curves in the reversible region which probes the shape of the gap near $T_c(H)$. Results of the analysis suggests that phase fluctuations are important in $Ba_{1-x}K_xFe_2As_2$ which is consistent with nodes in the gap.
The pairing mechanism in the iron-pnictide superconductors is still unknown. However, similarities to the cuprate high-temperature superconductors suggest that a similar mechanism may be at work. Recently, careful experimental studies of the spin exc
itation spectrum revealed, like in the cuprates, a strong temperature dependence in the normal state and a resonance feature in the superconducting state. Motivated by these findings, we develop a model of electrons interacting with a temperature dependent magnetic excitation spectrum based on these experimental observations. We apply it to analyse angle resolved photoemission and tunnelling spectra in Ba{1-x}KxFe2As2. We reproduce in quantitative agreement with experiment a renormalisation of the quasiparticle dispersion both in the normal and the superconducting state, and the dependence of the quasiparticle linewidth on binding energy. We estimate the strength of the coupling between electronic and spin excitations. Our findings support the possibility of a pairing mechanism based dominantly on such a coupling.
Resolving the microscopic pairing mechanism and its experimental identification in unconventional superconductors is among the most vexing problems of contemporary condensed matter physics. We show that Raman spectroscopy provides an avenue for this
quest by probing the structure of the pairing interaction at play in an unconventional superconductor. As we study the spectra of the prototypical Fe-based superconductor ${rm Ba_{1-x}K_xFe_2As_2}$ for $0.22le x le 0.70$ in all symmetry channels, Raman spectroscopy allows us to distill the leading $s$-wave state. In addition, the spectra collected in the $B_{1g}$ symmetry channel reveal the existence of two collective modes which are indicative of the presence of two competing, yet sub-dominant, pairing tendencies of $d_{x^2-y^2}$ symmetry type. A comprehensive functional Renormalization Group (fRG) and random-phase approximation (RPA) study on this compound confirms the presence of the two sub-leading channels, and consistently matches the experimental doping dependence of the related modes. The synopsis of experimental evidence and theoretical modelling supports a spin-fluctuation mediated superconducting pairing mechanism.
The reflectivity $R (omega)$ of $ab$-oriented Mg$_{1-x}$Al$_x$(B$_{1-y }$C$_y$)$_2$ single crystals has been measured by means of infrared microspectroscopy for $1300<omega<17000$ cm$^{-1}$. An increase with doping of the scattering rates in the $pi$
and $sigma$ bands is observed, being more pronounced in the C doped crystals. The $sigma$-band plasma frequency also changes with doping due to the electron doping, while the $pi$-band one is almost unchanged. Moreover, a $sigmatosigma$ interband excitation, predicted by theory, is observed at $omega_{IB} simeq 0.47$ eV in the undoped sample, and shifts to lower energies with doping. By performing theoretical calculation of the doping dependence $omega_{IB}$, the experimental observations can be explained with the increase with electron doping of the Fermi energy of the holes in the $sigma$-band. On the other hand, the $sigma$ band density of states seems not to change substantially. This points towards a $T_c$ reduction driven mainly by disorder, at least for the doping level studied here. The superconducting state has been also probed by infrared synchrotron radiation for $30<omega<150$ cm$^{-1}$ in one pure and one C-doped sample. In the undoped sample ($T_c$ = 38.5 K) a signature of the $pi$-gap only is observed. At $y$ = 0.08 ($T_c$ = 31.9 K), the presence of the contribution of the $sigma$-gap indicates dirty-limit superconductivity in both bands.
Single crystals of A$_{1-x}$K$_x$Fe$_2$As$_2$ (A=Ba, Sr) with high quality have been grown successfully by FeAs self-flux method. The samples have sizes up to 4 mm with flat and shiny surfaces. The X-ray diffraction patterns suggest that they have hi
gh crystalline quality and c-axis orientation. The non-superconducting crystals show a spin-density-wave (SDW) instability at about 173 K and 135 K for Sr-based and Ba-based compound, respectively. After doping K as the hole dopant into the BaFe$_2$As$_2$ system, the SDW transition is smeared, and superconducting samples with the compound of Ba$_{1-x}$K$_x$Fe$_2$As$_2$ (0 $< x leqslant$ 0.4) are obtained. The superconductors characterized by AC susceptibility and resistivity measurements exhibit very sharp superconducting transition at about 36 K, 32 K, 27 K and 23 K for x= 0.40,0.28,0.25 and 0.23, respectively.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها