تسجيل مستخدم جديدEffect of columnar defects on the pinning properties of NdFeAsO0.85 conglomerate particles
190
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
Oxypnictide superconductor NdFeAsO0.85 sample was irradiated with 2 GeV Ta ions at a fluence of 5x10^10 ions/cm2. High resolution transmission electron microscopy study revealed that the irradiation produced columnar-like defects. The effect of these defects on the irreversible magnetisation in polycrystalline randomly oriented fragments was studied as a function of field angle and field sweep rate. We find that the critical current density is enhanced at fields below the matching field (~1 Tesla) but only marginally. The pinning enhancement is anisotropic and maximum along the defect direction at high temperatures but the pinning then becomes more isotropic at low temperatures. The creep rate is suppressed at high temperatures and at fields below the matching field, indicating the columnar defects are efficient pinning sites at these H and T conditions.
قيم البحث
اقرأ أيضاً
Polycrystalline MgB2-xCx samples with x=0.05, 0.1, 0.2, 0.3, 0.4 nano-particle carbon powder were prepared using an in-situ reaction method under well controlled conditions to limit the extent of C substitution. The phases, lattice parameters, micros
tructures, superconductivity and flux pinning were characterized by XRD, TEM, and magnetic measurements. It was found that both the a-axis lattice parameter and the Tc decreased monotonically with increasing doping level. For the sample doped with the highest nominal composition of x=0.4 the Tc dropped only 2.7K. The nano-C-doped samples showed an improved field dependence of the Jc compared with the undoped sample over a wide temperature range. The enhancement by C-doping is similar to that of Si-doping but not as strong as for nano-SiC doped MgB2. X-ray diffraction results indicate that C reacted with Mg to form nano-size Mg2C3 and MgB2C2 particles. Nano-particle inclusions and substitution, both observed by transmission electron microscopy, are proposed to be responsible for the enhancement of flux pinning in high fields.
Here we use global and local magnetometry and Hall probe imaging to investigate the electromagnetic connectivity of the superconducting current path in the oxygen-deficient fluorine-free Nd-based oxypnictides. High resolution transmission electron mi
croscopy and scanning electron microscopy show strongly-layered crystallites, evidence for a ~ 5nm amorphous oxide around individual particles, and second phase neodymium oxide which may be responsible for the large paramagnetic background at high field and at high temperatures. From global magnetometry and electrical transport measurements it is clear that there is a small supercurrent flowing on macroscopic sample dimensions (mm), with a lower bound for the average (over this length scale) critical current density of the order of 103 A/cm2. From magnetometry of powder samples and local Hall probe imaging of a single large conglomerate particle ~120 microns it is clear that on smaller scales, there is better current connectivity with a critical current density of the order of 5 x 104 A/cm2. We find enhanced flux creep around the second peak anomaly in the magnetisation curve and an irreversibility line significantly below Hc2(T) as determined by ac calorimetry.
Transport characteristics of nano-sized superconducting strips and bridges are determined by an intricate interplay of surface and bulk pinning. In the limiting case of a very narrow bridge, the critical current is mostly defined by its surface barri
er, while in the opposite case of very wide strips it is dominated by its bulk pinning properties. Here we present a detailed study of the intermediate regime, where the critical current is determined, both, by randomly placed pinning centers and by the Bean-Livingston barrier at the edge of the superconducting strip in an external magnetic field. We use the time-dependent Ginzburg-Landau equations to describe the vortex dynamics and current distribution in the critical regime. Our studies reveal that while the bulk defects arrest vortex motion away from the edges, defects in their close vicinity promote vortex penetration, thus suppressing the critical current. We determine the spatial distribution of the defects optimizing the critical current and find that it is in general non-uniform and asymmetric: the barrier at the vortex-exit edge influence the critical current much stronger than the vortex-entrance edge. Furthermore, this optimized defect distribution has a more than 30% higher critical current density than a homogeneously disorder superconducting film.
The transverse Meissner effect (TME) in the highly layered superconductor $Bi_2Sr_2CaCu_2O_{8+y}$ with columnar defects is investigated by transport measurements. We present detailed evidence for the persistence of the Bose glass phase for $H_{perp}<
H_{perp c}$ : (i) the variable-range vortex hopping process for low currents crosses over to the half-loops regime for high currents; (ii) in both regimes near $H_{perp c}$ the energy barriers vanish linearly with $H_{perp}$ ; (iii) the transition temperature is governed by $T_{BG}(H_{parallel},0) -T_{BG}(H_{parallel},H_{perp}) sim |H_{perp}| ^{1/ u_{perp}}$ with $ u_{perp}=1.0 pm 0.1$. Furthermore, above the transition as $H_{perp}to H_{perp c}^+$, moving kink chains consistent with a commensurate-incommensurate transition scenario are observed. These results thereby clearly show the existence of the TME for $H_{perp}<H_{perp c}$ .
A series of polycrystalline SmFeAs1-xOx bulks was prepared to systematically investigate the influence of sample density on flux pinning properties. Different sample densities were achieved by controlling the pelletizing pressure. The superconducting
volume fraction, the critical current densities Jcm and the flux pinning force densities Fp were estimated from the magnetization measurements. Experimental results manifest that: (1) the superconducting volume fraction decreases with the decreasing of sample density. (2) The Jcm values have the similar trend except for the sample with very high density may due to different connectivity and pinning mechanism. Moreover, The Jcm(B) curve develops a peak effect at approximately the same field at which the high-density sample shows a kink. (3) The Fp(B) curve of the high-density sample shows a low-field peak and a high-field peak at several temperatures, which can be explained by improved intergranular current, while only one peak can be observed in Fp(B) of the low-density samples. Based on the scaling behaviour of flux pinning force densities, the main intragranular pinning is normal point pinning.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها