تسجيل مستخدم جديدMossbauer Spectroscopy Determination of iron foreign phases in the Superconducting Systems; RAsFeO1-x, RAsFeO1-xFx and Sr1-xKxFe2As2
87
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
The recently discovered superconducting - spin density wave materials, containing Fe and As, have raised huge interest. However most materials prepared to date, suffer from a varying degree of content of foreign Fe-As phases, Fe2As, FeAs2 and FeAs, which can lead to wrong conclusions concerning the properties of these materials. We show here that Mossbauer Spectroscopy is able to determine quite easily the relative content of the foreign phases. This procedure is demonstrated by a study of seven samples of superconducting or spin density wave materials, prepared in three different laboratories.
قيم البحث
اقرأ أيضاً
The recent discovery of superconductivity in oxypnictides with the critical temperature (TC) higher than McMillan limit of 39 K (the theoretical maximum predicted by Bardeen-Cooper-Schrieffer (BCS) theory) has generated great excitement. Theoretical
calculations indicate that the electron-phonon interaction is not strong enough to give rise to such high transition temperatures, while strong ferromagnetic/antiferromagnetic fluctuations have been proposed to be responsible. However, superconductivity and magnetism in pnictide superconductors show a strong sensitivity to the lattice, suggesting a possibility of unconventional electron-phonon coupling. Here we report the effect of oxygen and iron isotopic mass on Tc and the spin-density wave (SDW) transition temperature (TSDW) in SmFeAsO1-xFx and Ba1-xKxFe2As2 systems. The results show that oxygen isotope effect on TC and TSDW is very little, while the iron isotope exponent alpha=-dlnTc/dlnM is about 0.35, being comparable to 0.5 for the full isotope effect. Surprisingly, the iron isotope exchange shows the same effect on TSDW as TCc These results indicate that electron-phonon interaction plays some role in the superconducting mechanism, but simple electron-phonon coupling mechanism seems to be rather unlikely because a strong magnon-phonon coupling is included. Sorting out the interplay between the lattice and magnetic degrees of freedom is a key challenge for understanding the mechanism of high-TC superconductivity.
We report the temperature dependence of the transport critical current density (Jc) in textured Sr1-xKxFe2As2/Fe (Sr122) tapes fabricated by an ex situ powder-in-tube process. Critical currents were measured in magnetic fields up to 0-15 T and/or the
temperature range 4.2-30 K by using a dc four-probe method. It was found that textured Sr122 tapes heat-treated at low temperatures showed higher transport Jc performance due to much improved intergrain connections. At temperatures of 20 K, easily obtained using a cryocooler, Jc reached ~ 10^4 A/cm^2 in self field, which is the highest transport value of ferropnictide wires and tapes reported so far. Magneto-optical imaging observations further revealed significant and well distributed global Jc at 20 K in our tapes. These results demonstrate that 122 type superconducting tapes are promising for high-field applications at around 20 K.
We comparatively studied the critical current density, magnetization and specific heat of the rolled and the hot-pressed Sr1-xKxFe2As2 tapes. The Schottky anomaly that is obvious in the specific heat of the rolled tape disappears in the hot-pressed t
ape. Moreover, the hot-pressed tape has a higher fraction of superconductivity and a narrower distribution of superconducting transition temperature than the rolled tape. Combined with the magnetization data, we conclude that sintering under high pressure provides a better environment for complete chemical reaction and more homogenous dopant distribution, which is beneficial to the global current of a superconductor.
The superconducting gap in FeAs-based superconductor SmFeAs(O1-xFx) (x = 0.15 and 0.30) and the temperature dependence of the sample with x = 0.15 have been measured by Andreev reflection spectroscopy. The intrinsic superconducting gap is independent
of contacts while many other gap-like features vary appreciably for different contacts. The determined gap value of 2D = 13.34 +/-0.47 meV for SmFeAs(O0.85F0.15) gives 2D/kBTC = 3.68, close to the BCS prediction of 3.53. The superconducting gap decreases with temperature and vanishes at TC, in a manner similar to the BCS behavior but dramatically different from that of the nodal pseudogap behavior in cuprate superconductors.
The thermal conductivity kappa of the iron-arsenide superconductor Ba1-xKxFe2As2 was measured for heat currents parallel and perpendicular to the tetragonal c axis at temperatures down to 50 mK and in magnetic fields up to 15 T. Measurements were per
formed on samples with compositions ranging from optimal doping (x = 0.34; Tc = 39 K) down to dopings deep into the region where antiferromagnetic order coexists with superconductivity (x = 0.16; Tc = 7 K). In zero field, there is no residual linear term in kappa(T) as T goes to 0 at any doping, whether for in-plane or inter-plane transport. This shows that there are no nodes in the superconducting gap. However, as x decreases into the range of coexistence with antiferromagnetism, the residual linear term grows more and more rapidly with applied magnetic field. This shows that the superconducting energy gap develops minima at certain locations on the Fermi surface and these minima deepen with decreasing x. We propose that the minima in the gap structure arise when the Fermi surface of Ba1-xKxFe2As2 is reconstructed by the antiferromagnetic order.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها