We investigated the effect of using a synthetic ferrimagnetic (SyF) free layer in MgO-based magnetic tunnel junctions (MTJs) on current-induced magnetization switching (CIMS), particularly for application to spin-transfer torque random access memory (SPRAM). The employed SyF free layer had a Co40Fe40B20/ Ru/ Co40Fe40B20 and Co20Fe60B20/Ru/Co20Fe60B20 structures, and the MTJs(100x(150-300) nm^2) were annealed at 300oC. The use of SyF free layer resulted in low intrinsic critical current density (Jc0) without degrading the thermal-stability factor (E/kBT, where E, kB, and T are the energy potential, the Boltzmann constant, and temperature,respectively). When the two CoFeB layers of a strongly antiferromagnetically coupled SyF free layer had the same thickness, Jc0 was reduced to 2-4x10^6 A/cm^2. This low Jc0 may be due to the decreased effective volume under the large spin accumulation at the CoFeB/Ru. The E/kBT was over 60, resulting in a retention time of over ten years and suppression of the write current dispersion for SPRAM. The use of the SyF free layer also resulted in a bistable (parallel/antiparallel) magnetization configuration at zero field, enabling the realization of CIMS without the need to apply external fields to compensate for the offset field.
قيم البحث
اقرأ أيضاً
We report the intrinsic critical current density (Jc0) in current-induced magnetization switching and the thermal stability factor (E/kBT, where E, kB, and T are the energy potential, the Boltzmann constant, and temperature, respectively) in MgO base
d magnetic tunnel junctions with a Co40Fe40B20(2nm)/Ru(0.7-2.4nm)/Co40Fe40B20(2nm) synthetic ferrimagnetic (SyF) free layer. We show that Jc0 and E/kBT can be determined by analyzing the average critical current density as a function of coercivity using the Slonczewskis model taking into account thermal fluctuation. We find that high antiferromagnetic coupling between the two CoFeB layers in a SyF free layer results in reduced Jc0 without reducing high E/kBT.
Current-driven magnetization switching in low-resistance Co40Fe40B20/MgO/Co40Fe40B20 magnetic tunnel junctions (MTJs) is reported. The critical-current densities Jc required for current-driven switching in samples annealed at 270C and 300C are found
to be as low as 7.8 x 10^5 A/cm^2 and 8.8 x 10^5 A/cm^2 with accompanying tunnel magnetoresistance (TMR) ratios of 49% and 73 %, respectively. Further annealing of the samples at 350C increases TMR ratio to 160 %, while accompanying Jc increases to 2.5 x 10^6 A/cm^2. We attribute the low Jc to the high spin-polarization of tunnel current and small MsV product of the CoFeB single free layer, where Ms is the saturation magnetization and V the volume of the free layer.
The authors studied an effect of ferromagnetic (Co20Fe60B20 or Fe) layer insertion on tunnel magnetoresistance (TMR) properties of MgO-barrier magnetic tunnel junctions (MTJs) with CoFe/Pd multilayer electrodes. TMR ratio in MTJs with CoFeB/MgO/Fe st
ack reached 67% at an-nealing temperature (Ta) of 200 degree C and then decreased rapidly at Ta over 250 degree C. The degradation of the TMR ratio may be related to crystallization of CoFe(B) into fcc(111) or bcc(011) texture result-ing from diffusion of B into Pd layers. MTJs which were in-situ annealed at 350oC just after depo-siting bottom CoFe/Pd multilayer showed TMR ratio of 78% by post annealing at Ta =200 degree C.
The flow of in-plane current through ultrathin magnetic heterostructures can cause magnetization switching or domain wall nucleation owing to bulk and interfacial effects. Within the magnetic layer, the current can create magnetic instabilities via s
pin transfer torques (STT). At interface(s), spin current generated from the spin Hall effect in a neighboring layer can exert torques, referred to as the spin Hall torques, on the magnetic moments. Here, we study current induced magnetization switching in perpendicularly magnetized CoFeB/MgO heterostructures with a heavy metal (HM) underlayer. Depending on the thickness of the HM underlayer, we find distinct differences in the inplane field dependence of the threshold switching current. The STT is likely responsible for the magnetization reversal for the thinner underlayer films whereas the spin Hall torques cause the switching for thicker underlayer films. For the latter, we find differences in the switching current for positive and negative currents and initial magnetization directions. We find that the growth process during the film deposition introduces an anisotropy that breaks the symmetry of the system and causes the asymmetric switching. The presence of such symmetry breaking anisotropy enables deterministic magnetization switching at zero external fields.
Heterostructures composed of ferromagnetic layers that are mutually interacting through a nonmagnetic spacer are at the core of magnetic sensor and memory devices. In the present study, layer-resolved ferromagnetic resonance was used to investigate t
he coupling between the magnetic layers of a Co/MgO/Permalloy magnetic tunnel junction. Two magnetic resonance peaks were observed for both magnetic layers, as probed at the Co and Ni L3 x-ray absorption edges, showing a strong interlayer interaction through the insulating MgO barrier. A theoretical model based on the Landau-Lifshitz-Gilbert-Slonczewski equation was developed, including exchange coupling and spin pumping between the magnetic layers. Fits to the experimental data were carried out, both with and without a spin pumping term, and the goodness of the fit was compared using a likelihood ratio test. This rigorous statistical approach provides an unambiguous proof of the existence of interlayer coupling mediated by spin pumping.