تسجيل مستخدم جديدDiagonal and Collinear Incommensurate Spin Structures in underdoped La$_{2-x}$Ba$_{x}$CuO$_{4}$
112
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
We have studied incommensurate spin ordering in single crystal underdoped La_{2-x}Ba_{x}CuO_{4} with x~0.08, 0.05 and 0.025 using neutron scattering techniques. Static incommensurate magnetic order is observed in the La_{2-x}Ba_{x}CuO_{4} (x=0.05 and 0.025) compounds with ordering wavevectors which are rotated by 45 degree about the commensurate (0.5,0.5,0) position, with respect to that in the superconducting x=0.08 material. These spin modulations are one dimensional in the x=0.05 and 0.025 samples, with ordering wavevectors lying along the orthorhombic b* direction. Such a rotation in the orientation of the static spin ordering as a function of increasing Ba doping, from diagonal to collinear, is roughly coincident with the transition from an insulating to a superconducting ground state and is similar to that observed in the related La_{2-x}Sr_{x}CuO_{4} system. This phenomenon is therefore a generic property of underdoped La-214 cuprates.
قيم البحث
اقرأ أيضاً
We find excitations lower in energy than known phonon modes in underdoped La$_{2-x}$Sr$_x$CuO$_{4+delta}$ (x=0.08), with both inelastic X-Ray scattering (IXS) and inelastic neutron scattering (INS). A non dispersive excitation at 9 meV is identified
and is also seen by INS in (La,Nd)$_{2-x}$Sr$_x$CuO$_{4+delta}$, with 40$%$ Nd substitution. INS also identifies a still lower energy dispersive mode at low q in the Nd free sample. These modes are clearly distinct from the longitudinal acoustic phonon and correspond in energy to the Zone Centre modes measured by optical spectroscopy and associated with stripe dynamics.
We report detailed systematic measurements of the spatial variation in electronic states in the high T{c} superconductor La{2-x}Sr{x}CuO{4} (0.04<= x <= 0.16) using {63}Cu NQR for {63}Cu isotope enriched poly-crystalline samples. We demonstrate that
the spatial variation in local hole concentration {63}x{local} given by {63}x{local} = x +/- {63}Dx{local}, where x is the nominal hole concentration and {63}Dx{local} is defined as the amplitude (or extent) of the spatial variation, is reflected in the frequency dependence of the spin-lattice relaxation rate {63}1/T{1} across the inhomogeneous linebroadening of the {63}Cu NQR spectrum. By using high precision measurements of the temperature dependence of {63}1/T_{1} at various positions across the {63}Cu NQR lineshape, we demonstrate that {63}Dx{local} increases below 500 - 600 K and reaches values as large as {63}Dx{local} / x ~ 0.5 in the temperature region > 150 K. By incorporating the random positioning of {+2}Sr donor ions in the lattice in a novel approach, a lower bound to the length scale of the spatial variation {63}R{patch} is deduced by fitting the entire {63}Cu NQR spectrum (including the ``B -line) using a patch-by-patch distribution of the spatial variation {63}x{local} with the patch radius {63}R_{patch} > 3.0 nm as the only free parameter. A corresponding upper bound to the amplitude of the spatial variation {63}Dx{patch} (~ 1/{63}R_{patch}) is deduced within the model, and consistent results are found with {63}Dx{local} . We also deduce the onset temperature T{Q} (> 400 K) for local orthorhombic lattice distortions which, in the region x > 0.04, is found to be larger than the onset temperature of long range structural order.
We report incommensurate diffuse (ICD) scattering appearing in the high-temperature-tetragonal (HTT) phase of La$_{2-x}$(Sr,Ba)$_{x}$CuO$_{4}$ with $0.07 leq x leq 0.20$ observed by the neutron diffraction technique. For all compositions, a sharp sup
erlattice peak of the low-temperature-orthorhombic (LTO) structure is replaced by a pair of ICD peaks with the modulation vector parallel to the CuO$_6$ octahedral tilting direction, that is, the diagonal Cu-Cu direction of the CuO$_2$ plane, above the LTO-HTT transition temperature $T_s$. The temperature dependences of the incommensurability $delta$ for all samples scale approximately as $T/T_s$, while those of the integrated intensity of the ICD peaks scale as $(T-T_s)^{-1}$. These observations together with absence of ICD peaks in the non-superconducting $x=0.05$ sample evince a universal incommensurate lattice instability of hole-doped 214 cuprates in the superconducting regime.
The correlations between stripe order, superconductivity, and crystal structure in La(2-x)Ba(x)CuO(4) single crystals have been studied by means of x-ray and neutron diffraction as well as static magnetization measurements. The derived phase diagram
shows that charge stripe order (CO) coexists with bulk superconductivity in a broad range of doping around x=1/8, although the CO order parameter falls off quickly for x<>1/8. Except for x=0.155, the onset of CO always coincides with the transition between the orthorhombic and the tetragonal low temperature structures. The CO transition evolves from a sharp drop at low x to a more gradual transition at higher x, eventually falling below the structural phase boundary for optimum doping. With respect to the interlayer CO correlations, we find no qualitative change of the stripe stacking order as a function of doping, and in-plane and out-of-plane correlations disappear simultaneously at the transition. Similarly to the CO, the spin stripe order (SO) is also most pronounced at x=1/8. Truly static SO sets in below the CO and coincides with the first appearance of in-plane superconducting correlations at temperatures significantly above the bulk transition to superconductivity (SC). Indications that bulk SC causes a reduction of the spin or charge stripe order could not be identified. We argue that CO is the dominant order that is compatible with SC pairing but competes with SC phase coherence. Comparing our results with data from the literature, we find good agreement if all results are plotted as a function of x instead of the nominal x, where x represents an estimate of the actual Ba content, extracted from the doping dependence of the structural transition between the orthorhombic phase and the tetragonal high-temperature phase.
Recent angle resolved photoemission spectrascope (ARPES) experiments on strongly underdoped Bi$_2$Sr$_{2-x}$La$_x$CuO$_{6+delta}$ cuprates have reported an unusual gap in the nodal direction. Transport experiments on these cuprates found variable ran
ge hopping behavior observed. These cuprates have both electron and hole doping which has led to proposals that this cuprate is analogous to a partially compensated semiconductors. The nodal gap then corresponds to the Efros-Schklovskii(ES) gap in such semiconductors. We calculate the doping dependence and temperature dependence of a ES gap model and find support for an Efros-Schklovskii model.