تسجيل مستخدم جديدGraphene-on-Sapphire and Graphene-on-Glass: Raman Spectroscopy Study
197
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
The room-temperature Raman signatures from graphene layers on sapphire and glass substrates were compared with those from graphene on GaAs substrate and on the standard Si/SiO2 substrate, which served as a reference. It was found that while G peak of graphene on Si/SiO2 and GaAs is positioned at 1580 cm-1 it is down-shifted by ~5 cm-1 for graphene-on-sapphire (GOS) and, in many cases, splits into doublets for graphene-on-glass (GOG) with the central frequency around 1580 cm-1. The obtained results are important for graphene characterization and its proposed graphene applications in electronic devices.
قيم البحث
اقرأ أيضاً
We show the evolution of Raman spectra with number of graphene layers on different substrates, SiO$_{2}$/Si and conducting indium tin oxide (ITO) plate. The G mode peak position and the intensity ratio of G and 2D bands depend on the preparation of s
ample for the same number of graphene layers. The 2D Raman band has characteristic line shapes in single and bilayer graphene, capturing the differences in their electronic structure. The defects have a significant influence on the G band peak position for the single layer graphene: the frequency shows a blue shift upto 12 cm$^{-1}$ depending on the intensity of the D Raman band, which is a marker of the defect density. Most surprisingly, Raman spectra of graphene on the conducting ITO plates show a lowering of the G mode frequency by $sim$ 6 cm$^{-1}$ and the 2D band frequency by $sim$ 20 cm$^{-1}$. This red-shift of the G and 2D bands is observed for the first time in single layer graphene.
Graphene edges are of particular interest, since their chirality determines the electronic properties. Here we present a detailed Raman investigation of graphene flakes with well defined edges oriented at different crystallographic directions. The po
sition, width and intensity of G and D peaks at the edges are studied as a function of the incident light polarization. The D-band is strongest for light polarized parallel to the edge and minimum for perpendicular orientation. Raman mapping shows that the D peak is localized in proximity of the edge. The D to G ratio does not always show a significant dependence on edge orientation. Thus, even though edges can appear macroscopically smooth and oriented at well defined angles, they are not necessarily microscopically ordered.
We present an analysis of deep-UV Raman measurements of graphite, graphene and carbon nanotubes. For excitation energies above the strong optical absorption peak at the $M$ point in the Brillouin zone ($approx 4.7,text{eV}$), we partially suppress do
uble-resonant scattering processes and observe the two-phonon density of states of carbon nanomaterials. The measured peaks are assigned to contributions from LO, TO, and LA phonon branches, supported by calculations of the phonon dispersion. Moreover, we gain access to the infrared-active $E_{1u}$ mode in graphite. By lowering the excitation energy and thus allowing double-resonant scattering processes, we demonstrate the rise of the textit{2D} mode in graphite with ultra-short phonon wave vectors.
The graphene-enhanced Raman scattering of Rhodamine 6G molecules on pristine, fluorinated and 4-nitrophenyl functionalized graphene substrates was studied. The uniformity of the Raman signal enhancement was studied by making large Raman maps. The rel
ative enhancement of the Raman signal is demonstrated to be dependent on the functional groups, which was rationalized by the different doping levels of pristine, fluorinated and 4-nitrophenyl functionalized graphene substrates. The impact of the Fermi energy of graphene and the phonon energy of the molecules was considered together for the first time in order to explain the enhancement. Such approach enables to understand the enhancement without assuming anything about the uniformity of the molecules on the graphene surface. The agreement between the theory and our measured data was further demonstrated by varying excitation energy.
In this paper, we report our study on gold (Au) films with different thicknesses deposited on single layer graphene (SLG) as surface enhanced Raman scattering (SERS) substrates for the characterization of rhodamine (R6G) molecules. We find that an Au
film with a thickness of ~7 nm deposited on SLG is an ideal substrate for SERS, giving the strongest Raman signals for the molecules and the weakest photoluminescence (PL) background. While Au films effectively enhance both the Raman and PL signals of molecules, SLG effectively quenches the PL signals from the Au film and molecules. The former is due to the electromagnetic mechanism involved while the latter is due to the strong resonance energy transfer from Au to SLG. Hence, the combination of Au films and SLG can be widely used in the characterization of low concentration molecules with relatively weak Raman signals.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها